出発物質としてCO_2ガスを用いた炭化法による豊富な表面欠陥を持つMgOナノ結晶の合成【Powered by NICT】

Synthesis of MgO nanocrystals with abundant surface defects via a carbonization method employing CO₂ gas as starting material

著者 (23件)： Hai Chunxi (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Hai Chunxi (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Zhou Yuan (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Zhou Yuan (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Du Yongsheng (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Du Yongsheng (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Sun Yanxia (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Sun Yanxia (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Sun Yanxia (University of Chinese Academy of Sciences, Beijing 100049, China) ,  Zeng Jinbo (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Zeng Jinbo (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Shen Yue (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Shen Yue (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Ren Xiufeng (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Ren Xiufeng (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Ren Xiufeng (University of Chinese Academy of Sciences, Beijing 100049, China) ,  Li Xiang (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Li Xiang (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Zhang Lijuan (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Zhang Lijuan (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China) ,  Zhang Lijuan (University of Chinese Academy of Sciences, Beijing 100049, China) ,  Dong Ouyang (Key Laboratory of Comprehensive and Highly Effieicent Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, 18th Xinning Road, Xining 810008, China) ,  Dong Ouyang (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, China)
資料名： Materials Research Bulletin  (Materials Research Bulletin)
巻： 85  ページ： 181-187  発行年： 2017年 
JST資料番号： B0954A  ISSN： 0025-5408  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： そのユニークな性質を考慮して,主にこの研究における炭材としてCO_2ガスを採用した簡便なcarbnization法により合成した豊富な表面酸素欠陥を持つ均一に分散したMgOナノ粒子。60°Cで2時間の反応後に,Mg~2+イオンはMg_5(CO_3)4(OH)2(H_2O)4前駆体を毛虫好きに炭化した。また焼成中の脱炭と脱水プロセスを通じて,マイクロ-ナノ構造を有する調製したままのMg_5(CO_3)4(OH)2(H_2O)4前駆体はthouroughly高結晶性MgOナノ粒子に変換した。UV-VIS-NIR拡散反射分光法によるAs証明され,平均径の減少と共にコーナーとキンクサイトで大きく強化された低配位酸化物イオンのために,調製したままのMgOナノ結晶の禁制バンドギャップは5.3eVで,これは,種々の分野で興味深い応用付与である。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ヒ素 ,  ナノ粒子 ,  ナノ構造 ,  *酸化マグネシウム ,  前駆体 ,  結晶度 ,  *ナノ結晶 ,  バンドギャップ ,  脱炭 ,  *炭化 ,  脱水 ,  *表面欠陥 ,  酸化物イオン ,  拡散反射分光法 ,  酸素欠陥 ,  除去

著者キーワード (5件)： Aナノ構造 ,  A半導体 ,  B.光学的性質 ,  B結晶成長 ,  D.表面特性

分類 (1件)： 塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (5件)： 出発物質 ,  炭化法 ,  表面欠陥 ,  MgO ,  ナノ結晶