TI-25NB-25TA合金の引張変形過程における{332}<113>変形双晶のEBSD研究【JST・京大機械翻訳】

Study on {332}〈113〉deformtion twinning of Ti-25Nb-25Ta alloy during tensile deformation by EBSD

著者 (6件)： Hu Changqing (Institute of Microstructure and Property of Advanced Materials,Beijing University of Technology) ,  Liu Cuixiu (Institute of Microstructure and Property of Advanced Materials,Beijing University of Technology) ,  Chen Bin (Institute of Microstructure and Property of Advanced Materials,Beijing University of Technology) ,  Zhao Jie (Institute of Microstructure and Property of Advanced Materials,Beijing University of Technology) ,  Huang Zikun (Institute of Microstructure and Property of Advanced Materials,Beijing University of Technology) ,  Sun Wei (Institute of Microstructure and Property of Advanced Materials,Beijing University of Technology)
資料名： Dianzi Xianwei Xuebao  (Dianzi Xianwei Xuebao)
巻： 35  号： 5  ページ： 386-392  発行年： 2016年 
JST資料番号： W1469A  ISSN： 1000-6281  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 準安定Β型TI-25NB-25TA合金の室温引張変形における{332}<113>変形双晶の発展傾向と交差現象をEBSD技術を用いて研究した。結果は以下を示す。変形の増加とともに,双晶の幅は増加し,双晶の形態は,変形の初期段階で,直線から帯状に変化し,そして,変形の最終段階で,双晶は,変形し,そして,変形は,変形した。多くの結晶粒内に2種類以上の{332}<113>双晶変異体が発生し、一部の双晶エネルギーが連続的に成長し、いくつかの初回双晶内部に二次{332}<113>双晶が生じた。異なる変異体の双晶間には交差現象が起こりやすい。異なる{332}〈113〉双晶変異体の交差作用は交差領域に大きな局所格子歪みをもたらし、格子歪みは主に双晶内部に集中し、しかも交差界面での格子歪み程度は最も深刻である。交差効果の結果は,交差領域の結晶が異なる双晶変異体と基板の配向に対してある程度変化することを示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *変形双晶 ,  結晶粒 ,  格子歪 ,  合金 ,  *双晶 ,  界面 ,  *引張変形
準シソーラス用語： *EBSD , 【Automatic Indexing@JST】

著者キーワード (5件)： metastable β titanium alloy ,  room-temperature tensile deformation ,  EBSD ,  {332} 〈113〉deformation twinning ,  intersection phenomenon

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： 引張変形 ,  過程 ,  変形双晶 ,  EBSD ,  研究