超低溶接速度および回転速度を持つ大きな負荷を用いた摩擦撹はん溶接したCu継手の強度-延性相乗効果の達成【Powered by NICT】

Achieving good strength-ductility synergy of friction stir welded Cu joint by using large load with extremely low welding speed and rotation rate

著者 (5件)： Xu Nan (College of Mechanical and Electrical Engineering, Hohai University, Changzhou 213022, China) ,  Song Qining (College of Mechanical and Electrical Engineering, Hohai University, Changzhou 213022, China) ,  Bao Yefeng (College of Mechanical and Electrical Engineering, Hohai University, Changzhou 213022, China) ,  Jiang Yongfeng (College of Mechanical and Electrical Engineering, Hohai University, Changzhou 213022, China) ,  Shen Jun (College of Material Science and Engineering, Chongqing University, Chongqing 400044, China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 687  ページ： 73-81  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 厚さ2mmのCu板は非常に低い溶接速度と回転速度で大きな負荷摩擦撹拌溶接によって接合した。熱影響部は,改善された熱サイクルのための成功的に除去された。撹拌領域の結晶粒微細化は連続的な動的再結晶,不連続動的再結晶,動的回復と同様に双晶induce動的再結晶の組合せに起因した。撹拌領域は低転位密度を有する超微細粒と高傾角粒界の高い割合を示した。豊富な双晶境界は撹拌領域に導入した。その結果,撹拌領域は548MPaの強度と36%の一様伸びを持つ素晴らしい強度-延性相乗作用を示した。も延性損失なしに摩擦撹拌溶接したCu継手の強度を向上させる有効な戦略を提供した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 双晶 ,  双晶境界 ,  動的再結晶 ,  *摩擦撹拌溶接 ,  転位密度 ,  熱サイクル ,  伸び ,  *延性 ,  撹拌 ,  *溶接速度 ,  再結晶 ,  動的回復 ,  高傾角粒界 ,  結晶粒微細化 ,  *回転数

著者キーワード (6件)： Cu ,  摩擦撹はん溶接 ,  再結晶 ,  超微細粒子 ,  双晶 ,  機械的性質

分類 (3件)： 溶接部  (WC07100I) ,  機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (7件)： 溶接速度 ,  回転速度 ,  摩擦撹はん溶接 ,  Cu ,  継手 ,  延性 ,  相乗効果