J-GLOBAL ID：201702253543650651   整理番号：17A0754173

Ni基MMCコーティングに及ぼすCu_2S膜の耐摩耗効果【Powered by NICT】

Antifriction effects of Cu₂S film on Ni-based MMC coating

著者 (6件)： Zhao Jianbo (College of Mechanical and Electronic Engineering, China University of Petroleum, Qingdao 266580, China) ,  Zhao Jianbo (Department of Mechanics, QingDao Harbour Vocational and Technical College, Qingdao 266404, China) ,  Wang Yong (College of Mechanical and Electronic Engineering, China University of Petroleum, Qingdao 266580, China) ,  Han Bin (College of Mechanical and Electronic Engineering, China University of Petroleum, Qingdao 266580, China) ,  Li Meiyan (College of Mechanical and Electronic Engineering, China University of Petroleum, Qingdao 266580, China) ,  Cui Gang (College of Mechanical and Electronic Engineering, China University of Petroleum, Qingdao 266580, China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 315  ページ： 391-398  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 自己潤滑硫化物膜はそれらの顕著な性質と広範囲の応用に有望な機能のために関心が増している。本研究では,13μm厚さを持つ薄い硫化銅(Cu_2S)膜を低温イオン硫化によるNi55基板上に形成された摩耗と引裂きを減らすNi55被覆した。Cu_2S膜をSEMを用いた連続Cu_2Sナノシートから構築した多角形マイクロロッドから構成されている。膜の耐摩耗効果を,乾燥摩擦条件下で種々の負荷と速度を用いてボールオンディスク乾燥滑り試験を行った。結果はCu_2S膜は摩擦係数と摩耗深さを有意に減少させることにより強化された耐摩耗性能を示したことを示した。硫化第一銅と酸素による形成された銅粒子の助けを借りて,Cu_2S膜は互いに摩擦対を分離することができた。膜で被覆すること有意に摩耗を低減し,Ni55被覆からのデブリのプラウイング作用に起因する複合材料被覆に引き裂くことができた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ナノシート ,  自己潤滑 ,  摩擦係数 ,  低温 ,  *ニッケル ,  *被覆 ,  乾燥摩擦 ,  硫化銅 ,  耐摩耗性 ,  硫化 ,  *摩耗 ,  *銅 ,  酸素
準シソーラス用語： 乾燥滑り ,  マイクロロッド , 【Automatic Indexing@JST】

著者キーワード (6件)： 固体潤滑剤コーティング ,  減摩 ,  銅硫化物膜 ,  金属マトリックス複合材料 ,  レーザクラッディング ,  低温イオン硫化

分類 (1件)： 金属材料へのセラミック被覆  (YC02050V)

タイトルに関連する用語 (4件)： Ni基 ,  MMC ,  コーティング ,  耐摩耗