文献

J-GLOBAL ID：201702253738080256   整理番号：17A0095519

マイクロカプセル化NI/SFC3R触媒C5石の水素化反応【JST・京大機械翻訳】

Micro-size Eggshell-type Ni /SFC3R Catalyst for C5 Petroleum Resin Hydrogenation Reaction

著者 (6件)： Wei Caiqin (School of Chemistry and Chemical Engineering,Guangxi University) ,  Wang Linlin (School of Chemistry and Chemical Engineering,Guangxi University, Key Laboratory of Petrochemical Resources Processing and Process Intensification Technology of Guangxi) ,  Chen Xiaopeng (School of Chemistry and Chemical Engineering,Guangxi University, Key Laboratory of Petrochemical Resources Processing and Process Intensification Technology of Guangxi) ,  Pan Xiaoling (School of Chemistry and Chemical Engineering,Guangxi University) ,  Su Linlin (School of Chemistry and Chemical Engineering,Guangxi University) ,  Wang Yang (School of Chemistry and Chemical Engineering,Guangxi University)
資料名： Jingxi Huagong  (Jingxi Huagong)
巻： 33  号： 9  ページ： 1061-1068  発行年： 2016年 
JST資料番号： W1078A  ISSN： 1003-5214  CODEN： JIHUFJ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： NI/SFC3R触媒を,担体として流動化触媒分解触媒(SFC3R)を用いて,含浸法によって調製した。触媒の構造,表面相および還元性を,FIB(集束イオンビーム)-EDX,XRD,H_2-TPRおよびTEMによって特性評価した。C5石油樹脂の水素化に及ぼす反応温度,圧力,および時間の影響を研究し,そして,GARDNER5,レジン,GPC,FTIR,および1HNMRを用いて,加Qing改性5C樹脂の特性と構造を分析した。その結果,SFC3Rはゼオライト構造であり,NIの活性成分は主に担体の外側に分布し,NIOの平均粒径は21.5NMであり,良好な分散性を有することが判明した。C5石油樹脂の水素化の最適反応条件は以下の通りであった。温度280°C,圧力8.0MPA,時間5Hの条件下で,加Qing改性 C5石の色度は<1,色は水白色,硫黄含有量は<10MG/KG,価は0.45G BR/100Gであった。C5石油樹脂中の不飽和炭化水素はほぼ飽和しており,エッグ/NI/SFC3Rが優れたC5石油樹脂触媒水素化性能を有することを示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 還元性 ,  *石材 ,  反応温度 ,  流動化 ,  接触分解 ,  色度 ,  キャラクタリゼーション ,  *水素化 ,  含浸 ,  *触媒 ,  硫黄 ,  石油樹脂 ,  分散度
準シソーラス用語： 接触水素化 ,  反応条件 , 【Automatic Indexing@JST】

著者キーワード (5件)： eggshell-type catalyst ,  Ni /SFC3R ,  petroleum resin ,  hydrogenation ,  adhesives

分類 (2件)： 酸化,還元  (CF02060T) ,  その他の触媒  (CB06123Z)

タイトルに関連する用語 (5件)： マイクロカプセル化 ,  Ni ,  触媒 ,  C5 ,  水素化反応