B_2O_3 Bi_2O_3 SiO_2~-ZnOガラスの50wt%BaTiO_3の焼結挙動と特性研究【Powered by NICT】

Sintering behavior and characteristics study of BaTiO₃ with 50wt% of B₂O₃-Bi₂O₃-SiO₂-ZnO glass

著者 (4件)： Chen Mei-Yu (Microelectronics Research Unit, Faculty of Information Technology and Electrical Engineering, P.O. Box 4500, FI-90014, University of Oulu, Finland) ,  Juuti Jari (Microelectronics Research Unit, Faculty of Information Technology and Electrical Engineering, P.O. Box 4500, FI-90014, University of Oulu, Finland) ,  Hsi Chi-Shiung (Department of Material Science and Engineering, National United University, Miao-Li, 36003, Taiwan) ,  Jantunen Heli (Microelectronics Research Unit, Faculty of Information Technology and Electrical Engineering, P.O. Box 4500, FI-90014, University of Oulu, Finland)
資料名： Journal of the European Ceramic Society  (Journal of the European Ceramic Society)
巻： 37  号： 4  ページ： 1495-1500  発行年： 2017年 
JST資料番号： E0801B  ISSN： 0955-2219  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 異なる粒子サイズとLiFを添加したB_2O_3 Bi_2O_3 SiO_2~-ZnO(BBSZ)ガラスの熱分析はその温度挙動を研究するために研究した。次に50wt%BaTiO_3 50wt%BBSZガラスを有する複合材料は,収縮,微細構造及び誘電特性研究のために調製した。異なる処理をしたBBSZガラスは,より小さなガラス粒子は明らかにその軟化と結晶化温度を低下させることを示した。LiF添加は同じであったが非常に弱い影響を持っていた。複合材料は385 450°でBi_24Si_2O_40Cのガラス相と新しい相の発生,および680°C以上のBi_4BaTi_4O_15の軟化に関連した二段階収縮を示した。720°Cで焼結した複合材料の微細構造はBi_4BaTi_4O_15,BaTiO_3とBi_24Si_2O_40残留ZnO相を示した。LiF添加はBi_4BaTi_4O_15の量を増加し,損失値を増加させた。しかしガラスの粒径は,100kHzで複合材料248 256の誘電率と0.013の損失を示すの誘電特性に影響しなかった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 晶出温度 ,  *ガラス ,  複合材料 ,  粒径 ,  *焼結 ,  微細構造 ,  誘電率 ,  粒度 ,  誘電性 ,  *酸化亜鉛 ,  熱分析

著者キーワード (5件)： ガラス-セラミック複合材料 ,  BBSZ ,  BaTiO_3 ,  焼結挙動 ,  誘電特性

分類 (3件)： 誘電体一般  (BM05010F) ,  セラミック・磁器の性質  (YC03030G) ,  強誘電体,反強誘電体,強弾性  (BM05030B)

タイトルに関連する用語 (5件)： ZnO ,  ガラス ,  焼結 ,  挙動 ,  研究