表面結晶被覆によるバルク金属ガラスにおけるアニーリング誘起脆化の抑制【Powered by NICT】

Suppression of annealing-induced embrittlement in bulk metallic glass by surface crystalline coating

著者 (7件)： Chen Z.Q. (State Key Laboratory for Mechanical Behavior of Material, Xi’an Jiaotong University, Xi’an 710049, China) ,  Huang L. (State Key Laboratory for Mechanical Behavior of Material, Xi’an Jiaotong University, Xi’an 710049, China) ,  Wang F. (State Key Laboratory for Strength and Vibration of Mechanical Structures, Xi’an Jiaotong University, Xi’an 710049, China) ,  Huang P. (State Key Laboratory for Mechanical Behavior of Material, Xi’an Jiaotong University, Xi’an 710049, China) ,  Lu T.J. (State Key Laboratory for Strength and Vibration of Mechanical Structures, Xi’an Jiaotong University, Xi’an 710049, China) ,  Lu T.J. (MOE Key Laboratory for Multifunctional Materials and Structures, Xi’an Jiaotong University, Xi’an 710049, China) ,  Xu K.W. (State Key Laboratory for Mechanical Behavior of Material, Xi’an Jiaotong University, Xi’an 710049, China)
資料名： Materials & Design  (Materials & Design)
巻： 109  ページ： 179-185  発行年： 2016年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 自由体積(FV)の走行するために,金属ガラス(MGs)におけるアニーリング誘起脆化はそれらの実用的応用に有害であった。結晶W被覆を加えることにより,著者らは,熱力学的に,FVの好ましくないしたBMGから移動結晶にとして自由体積(FV)の大部分は,アニーリングによるZr_50 7Cu_28Ni_9Al_12バルク金属ガラス(BMG)中に保存されたおよび再分布できることを実証した。これに対応して,BMGの強度と延性は鋳造したままのものと比較して増強され,BMG中のZrとCuリッチクラスタの形成のような分解過程に起因していた。本研究の結果は,BMGにおけるアニーリング誘起脆化を回避し,強度とBMGの延性の両方を上昇させるための簡単で有効な手法を構築するのに適用できる可能性がある。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 再分布 ,  *被覆 ,  自由体積 ,  延性 ,  *バルク金属ガラス ,  *金属ガラス ,  ジルコニウム ,  *焼なまし ,  熱力学 ,  *結晶 ,  *脆化

著者キーワード (5件)： バルク金属ガラス ,  結晶コーティング ,  アニーリング ,  緩和 ,  自由体積

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 結晶 ,  バルク金属ガラス ,  アニーリング ,  誘起 ,  脆化