ヒドリドほう酸溶液の加水分解のための触媒としての室温固相反応によるポンポン状Co-Bナノ合金の調製【Powered by NICT】

Preparation of pompon-like Co-B nanoalloy by a room-temperature solid-state-reaction as a catalyst for hydrolysis of borohydride solution

著者 (5件)： Wang Xingpu (College of Chemistry and Chemical Engineering, Northwest Normal University, Lanzhou 730070, China) ,  Liao Jinyun (School of Chemistry and Materials Engineering, Huizhou University, Huizhou 516007, China) ,  Li Hao (School of Chemistry and Materials Engineering, Huizhou University, Huizhou 516007, China) ,  Wang Hui (College of Chemistry and Chemical Engineering, Northwest Normal University, Lanzhou 730070, China) ,  Wang Rongfang (College of Chemistry and Chemical Engineering, Northwest Normal University, Lanzhou 730070, China)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 42  号： 10  ページ： 6646-6656  発行年： 2017年 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 202.4m~2g~( 1)の大きな比表面積を有するナノシートから成るPomponのようなCo-B合金は容易な室温固相反応により合成した。合成におけるCoCl_26H_2OへのCO(NH_2)2の質量比を変えることにより,Co-B合金の形態を制御できる。これに対応して,比表面積は約43.4 202.4m~2g~( 1)から増加させることができる。ポンポン状Co-Bは,NaBH_4の加水分解のための触媒としての切断と,水素発生速度は8 26L水素分まで 1g触媒 1であることができる。この値は以前の報告で他の多くのCo-Bナノ合金のものと比較して大きかった。さらに,加水分解反応に対応する活性化エネルギーは25kJ/mol~ 1低く,ポンポン状Co-B触媒は優れた触媒性能を有していることを暗示した。ポンポン状Co-B合金は低コスト,良好な回復性と同様に,高い活性,水素生産のためのNaBH_4加水分解における実際的応用を見出す可能性があるという利点を有している。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *固相反応 ,  *合金 ,  *ヒドリドホウ酸 ,  活性化エネルギー ,  ヒドリドホウ酸ナトリウム ,  *加水分解 ,  触媒活性 ,  比表面積 ,  形態 ,  *触媒 ,  ナノシート
準シソーラス用語： 水素製造 ,  水素発生 ,  質量比 ,  *合金ナノ粒子 , 【Automatic Indexing@JST】