文献

J-GLOBAL ID：201702259730323592   整理番号：17A0301136

圧縮成形によるアルミニウム合金リングリングの残留応力の低減について研究した。【JST・京大機械翻訳】

Research on reduction of quenching residual stress for aluminum alloy ring by combination of tension and compression method

著者 (4件)： Wang Bingxiang (State Key Laboratory of High Performance Complex Manufacturing, School of Mechanical and Electrical Engineering, Central South University) ,  Yi Youping (State Key Laboratory of High Performance Complex Manufacturing, School of Mechanical and Electrical Engineering, Central South University) ,  Cui Jindong (State Key Laboratory of High Performance Complex Manufacturing, School of Mechanical and Electrical Engineering, Central South University) ,  Huang Shiquan (State Key Laboratory of High Performance Complex Manufacturing, School of Mechanical and Electrical Engineering, Central South University)
資料名： Zhongnan Daxue Xuebao Zirankexueban  (Zhongnan Daxue Xuebao Zirankexueban)
巻： 47  号： 10  ページ： 3381-3385  発行年： 2016年 
JST資料番号： C2798A  ISSN： 1672-7207  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 環状部品の焼入残留応力の問題を解決するために,焼入残留応力を削減するための新しい方法を提案した。この方法は,内側45°方向に圧力を印加することにより,引張と圧縮の効果を同時に生じる。有限要素ソフトウェアABAQUSを用いて,7085アルミニウム合金リングの残留応力と拉圧組合法の数値シミュレーションを行った。圧縮法を用いて,アルミニウム合金リングリングの残留応力の実験を行い,環状応力の変化をリングリング法により測定した。研究結果は以下を示す。リングの残留応力は主に断面の中央部に集中し,その最大応力は46MPAであった。高さ方向の変形が0.6%のとき,残留応力は約10MPAに減少した。圧力の増加とともに,残留応力は引張応力から圧縮応力に変化した。0.6%の変形を加えた環状体は,焼入れの間,2.26MMから0.34MMに変化し,実験結果はシミュレーション結果と一致した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *アルミニウム合金 ,  圧縮応力 ,  引張 ,  *残留応力 ,  環状体 ,  ソフトウェア ,  シミュレーション ,  *圧縮成形 ,  引張応力 ,  焼入 ,  最大応力 ,  数値シミュレーション ,  環状
準シソーラス用語： ABAQUS ,  有限要素 , 【Automatic Indexing@JST】

著者キーワード (4件)： ring ,  quenching residual stress ,  combination of tension and compression method ,  ring slitting method

分類 (2件)： 射出成形  (YH04050Y) ,  溶接部  (WC07100I)

タイトルに関連する用語 (4件)： 圧縮成形 ,  アルミニウム合金 ,  残留応力 ,  研究