その性質と応用のための亜鉛基板上の安定なIr ZnO/Zn超疎水性表面の作製【Powered by NICT】

Fabrication of stable Ir-ZnO/Zn superhydrophobic surface on zinc substrate for its properties and application

著者 (6件)： Wu Bei (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China) ,  Lu Shixiang (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China) ,  Xu Wenguo (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China) ,  Cui Shuo (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China) ,  Zhao Na (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China) ,  He Ge (School of Chemistry and Chemical Engineering, Beijing Institute of Technology, Beijing 100081, PR China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 699  ページ： 489-497  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 169°の水接触角と1°以下の滑り角をもつ集合組織化した氷エッジ型Ir ZnO/Zn超疎水性表面(SHS)はイリジウム(III)塩化物水溶液とアニーリング処理に垂直に加工した亜鉛シートを浸漬による亜鉛基板上に作製した。得られたSHSの形態と化学組成を走査電子顕微鏡(SEM),X線回折パターン(XRD)とX線光電子分光法(XPS)を用いて特性化した。Ir ZnO/Zn SHSは持続的安定性,優れた自浄能力,優れた耐食性,超浮力と同様に触媒の特性を示した。得られた試料の超浮力は亜鉛シートのそれの6.14倍であった。Ir ZnO/Zn SHSは光強度8Wの紫外線(UV)ランプで80分以内にメチルオレンジの完全な分解で良好な触媒活性を示した。さらに,Ir ZnO/Zn SHSはその触媒活性の著しい損失なしに最大3回リサイクル良好な安定性を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 走査電子顕微鏡 ,  集合組織 ,  触媒活性 ,  耐食性 ,  *亜鉛 ,  リサイクル ,  浮力 ,  浸漬 ,  X線光電子分光法 ,  化学組成 ,  焼なまし ,  スルホン酸 ,  芳香族アミン ,  アゾ化合物 ,  第三アミン
準シソーラス用語： 滑り角 ,  水接触角 ,  *超疎水性 , 【Automatic Indexing@JST】

著者キーワード (4件)： イリジウム ,  亜鉛 ,  光触媒 ,  超疎水性

分類 (1件)： 酸化物薄膜  (BK14050P)

物質索引 (1件)： メチルオレンジ

タイトルに関連する用語 (8件)： 性質 ,  応用 ,  亜鉛 ,  Ir ,  ZnO ,  Zn ,  超疎水性 ,  作製