テクスチャ表面上のグラフェン層の摩擦を減少させるための湿度の役割【Powered by NICT】

Role of humidity in reducing the friction of graphene layers on textured surfaces

著者 (5件)： Li Zheng-yang (Tribology Research Institute, Key Lab of Advanced Technologies of Materials, Southwest Jiaotong University, Chengdu, 610031, China) ,  Yang Wen-jing (Tribology Research Institute, Key Lab of Advanced Technologies of Materials, Southwest Jiaotong University, Chengdu, 610031, China) ,  Wu Yan-ping (China Academy of Engineering and Physics, Mianyang, 621900, China) ,  Wu Song-bo (Tribology Research Institute, Key Lab of Advanced Technologies of Materials, Southwest Jiaotong University, Chengdu, 610031, China) ,  Cai Zhen-bing (Tribology Research Institute, Key Lab of Advanced Technologies of Materials, Southwest Jiaotong University, Chengdu, 610031, China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 403  ページ： 362-370  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 多層グラフェンは摩擦と摩耗の低減に鋼表面上に作製した。グラフェンを含むエタノール溶液は鋼表面上に滴下し,エタノールを蒸発後数層グラフェンフレークの表面上に堆積した。グラフェンcontained表面(GCS)のトライボロジー性能を異なるRH(0%(乾燥窒素),30%,60%,および90%)におけるプレート接触に対する往復ボールにより誘導された。形態と摩耗痕をOM,2Dプロファイル,SEM,Raman分光法,およびXPSにより分析した。結果は,GCSは60%相対湿度(RH)の摩擦(COF)の摩耗係数を実質的に低減できることを示した。低COFは,摩擦界面に小さなせん断応力を与えるグラフェン層に起因して生じる。一方,高RHとテクスチャ表面の条件は,より長い時間持続する低いCOFとなるであろう。高含水量は炭素ダングリングボンドと水解離化学吸着による損傷からのグラフェンCネットワークを安定化し,保護することができると,組織化表面は,ディンプルに貯蔵された放出グラフェン層に起因していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 炭素 ,  *湿度 ,  界面 ,  ダングリングボンド ,  Raman分光法 ,  表面構造 ,  剪断応力 ,  蒸発 ,  解離吸着 ,  相対湿度 ,  摩耗 ,  含水量 ,  トライボロジー ,  *グラフェン ,  脂肪族アルコール

著者キーワード (4件)： グラフェン ,  摩擦と摩耗 ,  表面組織化 ,  湿度

分類 (2件)： その他の無機化合物の薄膜  (BK14060A) ,  炭素とその化合物  (YB02060D)

物質索引 (1件)： エタノール

タイトルに関連する用語 (5件)： テクスチャ ,  グラフェン ,  摩擦 ,  湿度 ,  役割