核形成剤TMC-210がポリ乳酸の結晶化と特性に及ぼす影響を研究した。【JST・京大機械翻訳】

Influence of Nucleator TMC-210 on Crystallization and Properties of PLLA

著者 (7件)： Ding Shengfang (Key Laboratory of Energy Resource and Chemical Engineering of Ningxia, Ningxia University) ,  Luo Faliang (Key Laboratory of Energy Resource and Chemical Engineering of Ningxia, Ningxia University) ,  Wang Kezhi (Shanxi Provincial Institute of Chemical Industry) ,  Xing Qian (School of Materials Science and Mechanical Engineering, Beijing Technology and Business University) ,  Si Pengfei (School of Materials Science and Mechanical Engineering, Beijing Technology and Business University) ,  Lei Xiaomei (School of Materials Science and Mechanical Engineering, Beijing Technology and Business University) ,  Shen Zhiyuan (School of Materials Science and Mechanical Engineering, Beijing Technology and Business University)
資料名： Gaofenzi Cailiao Kexue yu Gongcheng  (Gaofenzi Cailiao Kexue yu Gongcheng)
巻： 32  号： 10  ページ： 66-72  発行年： 2016年 
JST資料番号： C2119A  ISSN： 1000-7555  CODEN： GCKGEI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： PLLAの結晶化速度と衝撃強度が低いという問題を解決するために,PLLAの結晶化,溶融挙動,および機械的性質に及ぼす溶融混合物の影響を研究した。研究により、純L-ポリ乳酸(PLLA)は10°C/MINの冷却過程で結晶化せず、TMC-210の質量分率が0.2%の時、PLLAは著しく結晶化し、しかもTMC-210の含有量が増加するにつれ、結晶化は高温になることが分かった。等温結晶化の結果から,TMC-210の添加はPLLAの結晶化時間を短縮し,結晶化速度を増加させることがわかった。また,PLLAの核形成密度が増加し球晶サイズが減少するとともに,TMC-210質量分率が0.2%のとき,PLLAの衝撃強さは3.3倍向上した。そのため,TMC-210を添加することはPLLA結晶化と強靭化を促進する有効な核剤である。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 衝撃強さ ,  *ポリ乳酸 ,  機械的性質 ,  高温 ,  *結晶化 ,  晶析速度 ,  *核形成 ,  球晶
準シソーラス用語： 核剤 ,  強靱化 ,  等温結晶化 ,  質量分率 ,  冷却過程 ,  メルトブレンディング , 【Automatic Indexing@JST】

著者キーワード (4件)： poly(L-lactic acid) ,  crystallization ,  impact strength ,  TMC-210