NaCl酸性溶液中での純Alの不動態挙動へのLi添加の影響【Powered by NICT】

Influence of Li addition to passivity behavior of pure Al in NaCl acidic solution

著者 (5件)： Wang H. N. (Institute of Materials Science and Engineering, Shenyang Aerospace University, 37 Daoyi South Str., Shenyang, 110316, P. R. China) ,  Liu C. Z. (Institute of Materials Science and Engineering, Shenyang Aerospace University, 37 Daoyi South Str., Shenyang, 110316, P. R. China) ,  Lu L. (Institute of Materials Science and Engineering, Shenyang Aerospace University, 37 Daoyi South Str., Shenyang, 110316, P. R. China) ,  Li R. S. (Institute of Materials Science and Engineering, Shenyang Aerospace University, 37 Daoyi South Str., Shenyang, 110316, P. R. China) ,  Lin D. (Institute of Materials Science and Engineering, Shenyang Aerospace University, 37 Daoyi South Str., Shenyang, 110316, P. R. China)
資料名： Materials and Corrosion  (Materials and Corrosion)
巻： 68  号： 1  ページ： 58-64  発行年： 2017年 
JST資料番号： E0386A  ISSN： 0947-5117  CODEN： MTCREQ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 純Al,Al1Li合金,Al-2Li合金上の不動態膜は0.1mol/L NaCl酸性溶液(pH=2)で30分間potenyiostatic分極による 0.75V_SCEの不動態電位で形成された。不動態膜の腐食抵抗,半導体特性,および組成を電気化学インピーダンススペクトル(EIS),Mott-Schottky(M S)法,およびX線深さ光電子分光法(XPS)により,それぞれ,検討した。結果は純Alへの1と2wt%Li添加はその不動態性を改善し,特に2wt%Liであることを示した。さらに,Liは不動態膜生成プロセスに参加した。Al_2O_3の格子格子間位置における充填によるLi_2Oの導入は酸素空孔濃度を減少させることができるが,純粋なAl上の不動態膜のn型半導体特性を変化させなかった。受動性抵抗の増加は,酸素空格子点濃度の減少と純AlへのLi添加による不動態膜のFermiエネルギーの増加に起因した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 半導体 ,  *リチウム ,  光電子分光法 ,  分極 ,  *塩化ナトリウム ,  電気化学 ,  *アルミニウム ,  電位 ,  インピーダンススペクトル ,  合金 ,  耐食性 ,  *不動態 ,  不動態皮膜 ,  Fermi準位
準シソーラス用語： *酸性溶液 , 【Automatic Indexing@JST】

著者キーワード (4件)： Li添加 ,  取込 ,  不動態皮膜 ,  半導体特性

分類 (2件)： 腐食  (WB03030B) ,  防食  (WB03040M)

タイトルに関連する用語 (6件)： NaCl ,  酸性溶液 ,  純Al ,  不動態 ,  挙動 ,  Li