BiFeO3ナノチューブの合成とマルチフェロイック特性【Powered by NICT】

Synthesis and Multiferroic Properties of BiFeO3 Nanotubes

著者 (7件)： WANG Jing (Department of Electronic Science and Technology, School of Physical Science and Technology, Wuhan University) ,  LI Mei-Ya (Department of Electronic Science and Technology, School of Physical Science and Technology, Wuhan University) ,  LIU Xiao-Lian (Department of Electronic Science and Technology, School of Physical Science and Technology, Wuhan University) ,  PEI Ling (Department of Electronic Science and Technology, School of Physical Science and Technology, Wuhan University) ,  LIU Jun (Department of Electronic Science and Technology, School of Physical Science and Technology, Wuhan University) ,  YU Ben-Fang (Department of Electronic Science and Technology, School of Physical Science and Technology, Wuhan University) ,  ZHAO Xing-Zhong (Department of Electronic Science and Technology, School of Physical Science and Technology, Wuhan University)
資料名： Chinese Physics Letters  (Chinese Physics Letters)
巻： 26  号： 11  ページ： 188-191  発行年： 2009年 
JST資料番号： W1191A  ISSN： 0256-307X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 直径約200nm,長さ60μmを持つ高規則性BiFeOO3(BFO)ナノチューブをゾル-ゲル陽極酸化アルミニウム(AAO)テンプレート法により作製した。BFOのペロブスカイト型構造を透過型電子顕微鏡と制限視野電子回折分析によってナノチューブに確認された。室温でこれらのBFOナノチューブの強誘電と強磁性秩序の共存を実証し,26μC/cm~2の残留分極,60kV/cmの低い抗電場,および0.18emu/gの磁化を与えた。添加では,これらのナノチューブの漏れ挙動をOhm接触機構によって支配されていることが分かった。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 抗電場 ,  制限視野回折 ,  Ohm接触 ,  規則度 ,  残留分極 ,  *ナノチューブ ,  透過型電子顕微鏡
準シソーラス用語： 強磁性秩序 ,  ペロブスカイト型構造 ,  AAO【酸化物】 , 【Automatic Indexing@JST】