ガス透過性双方向調節可能な活性炭繊維/炭素複合膜の調製【JST・京大機械翻訳】

Preparation of activated carbon fibers/carbon composite membranes with dual-direction controllable gas permeability

著者 (7件)： Zhang Bing (School of Petrochemical Engineering, Shenyang University of Technology) ,  Zhou Jialing (School of Petrochemical Engineering, Shenyang University of Technology) ,  Wu Yonghong (School of Petrochemical Engineering, Shenyang University of Technology) ,  Li Lin (State key Lab of Fine Chemicals, School of Chemical Engineering, Dalian University of Technology) ,  Lu Yunhua (Provincial Key Laboratory of Functional Materials, University of Science and Technology Liaoning) ,  Bian Rui (School of Petrochemical Engineering, Shenyang University of Technology) ,  Wang Tonghua (State key Lab of Fine Chemicals, School of Chemical Engineering, Dalian University of Technology)
資料名： Huaxue Gongcheng  (Huaxue Gongcheng)
巻： 44  号： 11  ページ： 60-64  発行年： 2016年 
JST資料番号： C2007A  ISSN： 1005-9954  CODEN： HUGOEN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 3,3’,4,4’-ジフェニルエーテル-4,4’-ジアミノ(ODPA-ODA)ポリエーテルを前駆体として,活性炭繊維(ACF)をドーパントとして,ACF/C/複合複合膜を調製した。膜の熱安定性,表面官能基,表面形態,および微細構造を,熱重量分析,赤外分光法,走査型電子顕微鏡,およびX線回折によって特性評価した。前駆体膜と炭素膜の構造と特性に及ぼすACFの量の影響を研究した。結果は,ACFの導入が前駆体の熱安定性を改善することを示した。ACFの量が0から0.5%に増加すると,炭素膜の細孔径はそれぞれブロッキング%と形成%に増加し,ガス透過性は最初に減少し,次に増加した。炭素膜と比較して,ACFの量が0.5%のとき,H_2,CO_2,O_2およびN_2の透過性は,それぞれ1.5倍,18.6倍,5.3倍および5.8倍増加した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 熱安定性 ,  ブロッキング ,  熱重量分析 ,  *複合膜 ,  キャラクタリゼーション ,  前駆体 ,  *透気性 ,  走査電子顕微鏡 ,  ドーパント ,  細孔径 ,  *活性炭
準シソーラス用語： *透過性 ,  炭素膜 ,  表面形態 ,  官能基 , 【Automatic Indexing@JST】

著者キーワード (4件)： polyetherimide ,  carbon membranes ,  activated carbon fiber ,  permeability