Effect of LaB₆ content on the gas evolution and structure of ZrC coating for carbon/carbon composites during ablation

著者 (5件)： Jia Yujun (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, PR China) ,  Li Hejun (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, PR China) ,  Yao Xiyuan (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, PR China) ,  Zhao Zhigang (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, PR China) ,  Sun Jiajia (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 4  ページ： 3601-3609  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： SiC被覆炭素/炭素複合材料のためのLaB_6の含有量が異なるZrC皮膜は超音速大気プラズマ溶射により作製した。超高温での酸化中にガス発生および含有量が異なるLaB_6の添加後の皮膜の酸化物スケール構造進展の機構を研究した。結果は希土類ホウ酸塩よりも希土類酸化物は主に酸化スケールの融解抵抗を低下させることを示した。10%LaB_6のZrC被覆のための酸化物スケールはガス回避に好ましくなかった。20%LaB_6を添加した後,酸化物スケールはガス脱出するには都合が良いが減少された溶解抵抗のために,洗掘を含む環境に適用した被覆に不利である。LaB_6の高含量もB_2O_3の明らかな沸騰を引き起こし,アブレーション中の酸化物スケールに大きな細孔を生成した。ZrC被覆のLaB_6の適切な含有量は15%であることが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 細孔 ,  酸化物 ,  酸化膜 ,  *アブレーション ,  希土類元素 ,  炭化ケイ素 ,  超高温 ,  *C/C複合材料 ,  ホウ酸塩 ,  皮膜 ,  酸化
準シソーラス用語： 希土類酸化物 ,  大気プラズマ溶射 ,  超音速 ,  *ガス発生 , 【Automatic Indexing@JST】

著者キーワード (4件)： Carbides ,  塗料 ,  酸化 ,  希土類化合物