文献

J-GLOBAL ID：201702271356772499   整理番号：17A0375586

CoドープαFe00Hの低温脱硫:相組成の調整と欠陥の生成【Powered by NICT】

Low temperature desulfurization on Co-doped α-FeOOH: Tailoring the phase composition and creating the defects

著者 (5件)： Cao Yanning (National Engineering Research Center of Chemical Fertilizer Catalyst, Fuzhou University, Fuzhou, Fujian 350002, China) ,  Shen Lijuan (National Engineering Research Center of Chemical Fertilizer Catalyst, Fuzhou University, Fuzhou, Fujian 350002, China) ,  Hu Xiaoli (National Engineering Research Center of Chemical Fertilizer Catalyst, Fuzhou University, Fuzhou, Fujian 350002, China) ,  Du Zhongjie (National Engineering Research Center of Chemical Fertilizer Catalyst, Fuzhou University, Fuzhou, Fujian 350002, China) ,  Jiang Lilong (National Engineering Research Center of Chemical Fertilizer Catalyst, Fuzhou University, Fuzhou, Fujian 350002, China)
資料名： Chemical Engineering Journal  (Chemical Engineering Journal)
巻： 306  ページ： 124-130  発行年： 2016年 
JST資料番号： D0723A  ISSN： 1385-8947  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本論文では,一連のCoドープαFe00H(針鉄鉱)を簡単な共沈法によって調製した。得られた試料は粉末X線回折(XRD),N_2吸着-脱着等温線,X線光電子分光法(XPS),走査電子顕微鏡(SEM),Raman分光法および電子スピン共鳴(ESR)により詳細に特性化した。H_2S吸着実験は,CoドープαFe00H試料を低温(25°C)で著しく高いブレークスルー硫黄容量を示した。最大数はCo/Fe=0.07で53.2%,これはドープしていないαFe00H試料のそれと比べてはるかに高くに達した。改善された活性は主にαFe00Hの大きな表面積とαFe00H構造へのCo~2+の混入に起因する酸素空孔のような格子欠陥の増加に起因すると考えられる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 針鉄鉱 ,  *低温 ,  走査電子顕微鏡 ,  共沈 ,  硫黄 ,  Raman分光法 ,  X線回折 ,  表面積 ,  等温線 ,  *相組成 ,  ESR【磁気共鳴】 ,  *ドーピング ,  X線光電子分光法
準シソーラス用語： 酸素空格子点 ,  粉末X線回折 , 【Automatic Indexing@JST】

著者キーワード (4件)： αFe00H ,  金属ドーピング ,  低温脱硫 ,  酸素空格子点

分類 (2件)： 下水,廃水の化学的処理  (SC03050W) ,  触媒操作  (XE01050T)

タイトルに関連する用語 (6件)： CO ,  ドープ ,  低温 ,  脱硫 ,  相組成 ,  欠陥