処理したZn含有電気アーク炉ダストから金属をドープしたNi-Znフェライトの容易な合成【Powered by NICT】

Facile synthesis of metal-doped Ni-Zn ferrite from treated Zn-containing electric arc furnace dust

著者 (5件)： Wang Hui-gang (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China) ,  Liu Wenwu (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China) ,  Jia Nannan (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhang Mei (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China) ,  Guo Min (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 2  ページ： 1980-1987  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： スピネル構造を持つ金属ドープNi-Znフェライトを直接固相反応法によって処理された亜鉛含有電気アーク炉ダスト(Zn含有EAFD)から合成した高付加価値材料への固体廃棄物の変換を実現した。NiCl_26H_2Oは焼成前に処理したZn含有EAFDに添加した。NiCl_26H_2O(R_TZE/N,gg~( 1))に処理したZn含有EAFDの質量比と合成と合成したままの試料の磁気的性質に及ぼすか焼温度の影響をX線回折,Raman分光法および物理的性質測定により系統的に調べた。R_TZE/Nと焼成温度は単相スピネルフェライトとその磁気的性質の合成に著しく影響することが判明した。焼成温度は,1:0.9のR_TZE/Nで2時間,1100°Cで制御したとき,高い飽和磁化(Ms,60.5emug~( 1))と低い保磁力(Hc, 49.8Oe)の良好な磁気特性を示し,純粋な金属をドープしたNi-Znフェライトが得られた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 単相 ,  *亜鉛 ,  *塵埃 ,  X線回折 ,  固相反応 ,  飽和磁化 ,  *ドーピング ,  Raman分光法 ,  保磁力 ,  磁気的性質 ,  *フェライト ,  *アーク炉
準シソーラス用語： 焼成温度 ,  か焼温度 ,  スピネル型構造 , 【Automatic Indexing@JST】

著者キーワード (4件)： Zn含有EAFD ,  固相反応 ,  金属ドープNi-Znフェライト ,  磁気特性