液体シンチレータ中に浸漬したPMMAのクリープ挙動と寿命予測【Powered by NICT】

Creep behavior and lifetime prediction of PMMA immersed in liquid scintillator

著者 (6件)： Zhou Fan (Institute of Process Equipment, College of Chemical and Biological Engineering, Zhejiang University, Hangzhou 310027, China) ,  Hou Shaojing (Institute of High Energy Physics Chinese Academy of Sciences, Beijing 100049, China) ,  Qian Xiaohui (Institute of High Energy Physics Chinese Academy of Sciences, Beijing 100049, China) ,  Chen Zhiping (Institute of Process Equipment, College of Chemical and Biological Engineering, Zhejiang University, Hangzhou 310027, China) ,  Zheng Chenchao (Institute of Process Equipment, College of Chemical and Biological Engineering, Zhejiang University, Hangzhou 310027, China) ,  Xu Feng (Institute of Process Equipment, College of Chemical and Biological Engineering, Zhejiang University, Hangzhou 310027, China)
資料名： Polymer Testing  (Polymer Testing)
巻： 53  ページ： 323-328  発行年： 2016年 
JST資料番号： C0752B  ISSN： 0142-9418  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 室温で液体シンチレータに浸漬したPMMAのクリープ挙動は新しいタイプのクリープ試験機を用いて実験的に研究した。八応力レベルで短期およびクリープ破断両方の引張試験を行った。参照応力でのクリープコンプライアンスのマスタ曲線は時間ストレス重ね合わせ原理に従って得られた。マスター曲線は,実際の長期クリープ曲線と比較した。二つの曲線は短時間で良く一致することを示した。しかし,時間が進行すると実際のクリープデータは,より高いクリープ速度を示した。実際の寿命はマスター曲線によって予測されたものよりもはるかに短かった。さらに,長期クリープで制限される強度と寿命の間の関係を決定した。結果はニュートリノ観測所への応用のためのPMMA容器の安全設計を導くために使用することができる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *浸漬 ,  *クリープ ,  クリープ破断 ,  重合せ ,  引張試験 ,  *寿命予測 ,  *ポリメタクリル酸メチル ,  *液体シンチレータ ,  クリープ速度 ,  クリープ試験 ,  安全設計
準シソーラス用語： クリープ曲線 ,  マスタ曲線 ,  クリープコンプライアンス ,  *クリープ挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： クリープ ,  PMMA ,  時間-応力重ね合わせ原理 ,  マスター曲線 ,  寿命予測

分類 (1件)： ゴム・プラスチック材料  (HC06030K)

タイトルに関連する用語 (5件)： 液体シンチレータ ,  浸漬 ,  PMMA ,  クリープ挙動 ,  寿命予測