反応結合炭化けい素のセラミック射出成形に及ぼす炭素含有量の影響【Powered by NICT】

Influence of Carbon Content on Ceramic Injection Molding of Reaction-Bonded Silicon Carbide

著者 (14件)： Zhang Zhao (Key Laboratory for Liquid-Solid Structural Evolution & Processing of Materials of Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Zhang Zhao (Key Laboratory of Special Functional Aggregated Materials, Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Zhang Yujun (Key Laboratory for Liquid-Solid Structural Evolution & Processing of Materials of Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Zhang Yujun (Key Laboratory of Special Functional Aggregated Materials, Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Gong Hongyu (Key Laboratory for Liquid-Solid Structural Evolution & Processing of Materials of Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Gong Hongyu (Key Laboratory of Special Functional Aggregated Materials, Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Guo Xue (Key Laboratory for Liquid-Solid Structural Evolution & Processing of Materials of Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Guo Xue (Key Laboratory of Special Functional Aggregated Materials, Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Zhang Yubai (Key Laboratory for Liquid-Solid Structural Evolution & Processing of Materials of Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Zhang Yubai (Key Laboratory of Special Functional Aggregated Materials, Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Wang Xianli (Key Laboratory for Liquid-Solid Structural Evolution & Processing of Materials of Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Wang Xianli (Key Laboratory of Special Functional Aggregated Materials, Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Yu Jincheng (Key Laboratory for Liquid-Solid Structural Evolution & Processing of Materials of Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China) ,  Yu Jincheng (Key Laboratory of Special Functional Aggregated Materials, Ministry of Education, Shandong University, Jinan, 250061, People’s Republic of China)
資料名： International Journal of Applied Ceramic Technology  (International Journal of Applied Ceramic Technology)
巻： 13  号： 5  ページ： 838-843  発行年： 2016年 
JST資料番号： W1929A  ISSN： 1546-542X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 反応結合炭化ケイ素(RBSC)は炭化ケイ素(SiC),ワックスベースの有機系と種々の量のカーボンブラックを含む原料を用いたセラミック射出成形(CIM)法により調製した。反応焼結プロセスの重要な効果として,炭素はカーボンブラックと有機高分子の分解生成物からそれぞれ導入した。有機物の熱分解のプロセスに大きな役割を果たしているので,この研究では,まず混合と注入過程に及ぼす炭素含有量の影響を記述し,次に脱バインダプロセスを強調した。結果は,望ましい熱的脱バインダーがN_2で実施し,最適性能はカーボンブラックの7wt.%のRBSCで得られ,2.98g/~3,見掛け気孔率0.24%,曲げ強さ301.59MPa,破壊靭性4.18MPa m~1/2の密度を持つことを示した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 熱分解 ,  破壊靱性 ,  高分子 ,  *炭化ケイ素 ,  粘結剤 ,  カーボンブラック ,  分解物 ,  *セラミック ,  反応焼結 ,  有機物 ,  *射出成形 ,  曲げ強さ ,  *炭素
準シソーラス用語： 見掛け気孔率 ,  *炭素量 , 【Automatic Indexing@JST】

著者キーワード (4件)： 炭化けい素 ,  炭素含有量 ,  射出成形 ,  脱バインダ