熱間圧延Mo含有鋼における微細構造進化,析出挙動と引張特性に及ぼすNbとVの影響【Powered by NICT】

Effects of Nb and V on Microstructural Evolution, Precipitation Behavior and Tensile Properties in Hot-rolled Mo-bearing Steel

著者 (5件)： Liu Fuming (School of Materials Science and Engineering, Northeastern University) ,  Wang Jianjun (School of Materials Science and Engineering, Northeastern University) ,  Liu Yujie (School of Materials Science and Engineering, Northeastern University) ,  Misra R D K (Laboratory for Excellence in Advanced Steel Research, Department of Metallurgical and Materials Engineering, University of Texas at El Paso) ,  Liu Chunming (School of Materials Science and Engineering, Northeastern University)
資料名： Journal of Iron and Steel Research, International  (Journal of Iron and Steel Research, International)
巻： 23  号： 6  ページ： 560-565  発行年： 2016年 
JST資料番号： W1513A  ISSN： 1006-706X  CODEN： GAYXEN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 四実験Mo含有鋼のミクロ組織の発達,析出挙動と引張特性は微細構造特性に及ぼすNbとVの効果を解明するために研究した。結果は,熱間圧延鋼のミクロ組織は多角形フェライトと縮退パーライトから構成されていたことを示し,形態は600°Cで1時間保持した後同じままであった。最小粒径はNb V Moを含む鋼,Nb-Mo及びV-Mo鋼であった。降水量は熱間圧延Mo含有鋼で少なかった。析出物の最大体積分率はNb V Mo軸受鋼で得られ,Nb V Mo錯体炭窒化物は,600°Cで非常に安定であった。Mo含有鋼では,降伏比は室温で最低であったが600°C,転位運動に及ぼすMo炭化物の析出とMo溶質のドラッグ効果に起因するで最も高かった。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： *ニオブ ,  *鋼 ,  炭化物 ,  析出物 ,  *モリブデン ,  パーライト ,  溶質 ,  体積率 ,  粒径 ,  軸受鋼 ,  フェライト ,  *熱間圧延
準シソーラス用語： 炭窒化物 ,  *引張特性 , 【Automatic Indexing@JST】

著者キーワード (4件)： Mo含有鋼 ,  微細構造進化 ,  高温強度 ,  沈殿

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： 熱間圧延 ,  Mo ,  微細構造進化 ,  析出 ,  挙動 ,  引張特性 ,  Nb