ポリ(エチレンテレフタラート-co-ナトリウム-5-スルホ-iso-フタラート)の非等温融解-結晶化速度論【Powered by NICT】

Non-isothermal melt-crystallization kinetics of poly (ethylene terephthalate-co-sodium-5-sulfo-iso-phthalate)

著者 (6件)： Wang Lipeng (School of Chemistry and Chemical Engineering, Harbin Institute of Technology, Harbin, 150001, China) ,  Wang Lipeng (School of Chemical and Chemistry, Nantong University, Nantong, 226019, China) ,  Zhang Fucheng (School of Chemistry and Chemical Engineering, Harbin Institute of Technology, Harbin, 150001, China) ,  Zhang Fucheng (School of Chemical and Chemistry, Nantong University, Nantong, 226019, China) ,  Bai Yongping (School of Chemistry and Chemical Engineering, Harbin Institute of Technology, Harbin, 150001, China) ,  Ding Liping (School of Chemical and Chemistry, Nantong University, Nantong, 226019, China)
資料名： Thermochimica Acta  (Thermochimica Acta)
巻： 645  ページ： 43-49  発行年： 2016年 
JST資料番号： E0350C  ISSN： 0040-6031  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ポリ(エチレンテレフタラート-co-ナトリウム-5-スルホ-iso-フタラート)(PETI)の非等温結晶化の動力学を示差走査熱量測定(DSC)を用いて調べた。各種マクロ動力学モデル,すなわち,Avrami,Tobin,Ozawa,ZiabickiはPETIの非等温結晶化過程を記述するために使用した。Avrami結晶化速度定数とTobin結晶化速度定数の両方は,冷却速度の増加と共に増加することを観察した。AvramiモデルであるPETIの非等温結晶化過程を記述するためにTobinモデルより優れていた。Ozawa結晶化速度K_Oは冷却速度の増加とともに減少することが分かったが,Ziabickiの速度論的結晶パラメータG_Zは冷却速度の増加と共に増加することが分かった。Friedmanの微分等変換法に基づいて解析し,PETIの非等温結晶化過程の有効エネルギー障壁△Eは相対結晶化度の増加関数であることが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 微分 ,  示差走査熱量測定 ,  冷却速度 ,  結晶度 ,  *速度論 ,  *晶析速度 ,  *結晶化 ,  *結晶
準シソーラス用語： 速度定数 ,  動力学モデル ,  非等温結晶化 , 【Automatic Indexing@JST】

著者キーワード (3件)： ポリ(エチレンテレフタラート-co-ナトリウム-5-スルホ-iso-フタラート) ,  非等温融解-結晶化過程 ,  マクロ動力学モデル

分類 (2件)： 高分子固体の構造と形態学  (CG02022M) ,  高分子溶液の物理的性質  (CG02013S)

タイトルに関連する用語 (6件)： エチレン ,  テレフタラート ,  ナトリウム ,  フタラート ,  融解 ,  結晶化速度論