上昇した温度での3次元4段階編みSiC/SiC複合材料の引張クリープ挙動【Powered by NICT】

Tensile creep behavior of three-dimensional four-step braided SiC/SiC composite at elevated temperature

著者 (8件)： Jing Xin (School of Power and Energy, Northwestern Polytechnical University, Xi’an 710072, China) ,  Jing Xin (School of Energy and Power Engineering, Beihang University, Beijing 100191, China) ,  Yang Xiaoguang (School of Energy and Power Engineering, Beihang University, Beijing 100191, China) ,  Yang Xiaoguang (Collaborative Innovation Center of Advanced Aero-engine, Beijing 100191, China) ,  Shi Duoqi (School of Energy and Power Engineering, Beihang University, Beijing 100191, China) ,  Shi Duoqi (Collaborative Innovation Center of Advanced Aero-engine, Beijing 100191, China) ,  Shi Duoqi (Beijing Key Laboratory of Aero-Engine Structure and Strength, Beijing 100191, China) ,  Niu Hongwei (China Flight Test Establishment, Xi’an China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 9  ページ： 6721-6729  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文では,空気中1100°Cと1300°Cでの三次元四段階編組したSiC/SiC複合材料の引張クリープ変形と破断挙動に対する実験結果を提示した。1300°Cでのクリープ挙動は長い過渡クリープ領域を示し,クリープ速度は時間と共に連続的に減少した。1100°Cでのクリープ挙動は,見かけの一定割合の領域を示し,クリープ変形は1300°Cでのそれよりも小さかった。しかし,両温度でのクリープ破断時間はほとんど差を示さなかった。クリープ変形と破断挙動を制御する機構を解析した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *複合材料 ,  *クリープ ,  *三次元 ,  編組 ,  クリープ速度 ,  クリープ破断 ,  *引張 ,  破断
準シソーラス用語： *引張クリープ ,  *クリープ挙動 ,  *SiC/SiC複合材料 , 【Automatic Indexing@JST】

著者キーワード (4件)： SiC/SiC複合材料 ,  クリープ ,  破壊 ,  セラミックマトリックス複合材料

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (6件)： 3次元 ,  段階 ,  SiC ,  複合材料 ,  引張 ,  クリープ挙動