その場重合により,ポリエステル/リン酸塩ガラス複合材料の構造と特性を研究した。【JST・京大機械翻訳】

Study on the structure and property of phosphorus flame retardant copolyester/P-glass nanocomposite by in-situ polymerization

著者 (4件)： Fu Sicong (State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Sicence and Engineering,Donghua University) ,  Fang Kai (State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Sicence and Engineering,Donghua University) ,  Ma Jinghong (State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Sicence and Engineering,Donghua University) ,  Gong Jinghua (State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Sicence and Engineering,Donghua University)
資料名： Huagong Xinxing Cailiao  (Huagong Xinxing Cailiao)
巻： 44  号： 12  ページ： 49-52  発行年： 2016年 
JST資料番号： C2923A  ISSN： 1006-3536  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： _(CEPPA)/リン酸塩ガラス(P-GLASS)ナノ複合材料を,第三単量体として2-カルボキシエチル(CEPPA)を用いて,その場重合によって調製した。それらの構造と特性を元素分析,DSC,TGA,限界酸素指数,垂直燃焼によって研究した。結果は以下を示す。その場重合過程において,P-GLASSはマトリックス内でナノサイズの均一分散を示し,阻燃共の分子鎖と相互作用した。P-GLASSのIN SITU添加は,複合材料の熱安定性を改良し,溶融粘度を低下させ,固有粘度は0.64DL/G,FRPET/P-GLASSの含有量は8.194MG/G,そして,PGLASSの含有量は1%以上であった。FRPET/P-GLASSの垂直燃焼性能レベルはFV-0級に達し、極酸素指数は30.9%に達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 相互作用 ,  *リン酸塩ガラス ,  酸素指数 ,  元素分析 ,  熱安定性 ,  *複合材料 ,  ナノ複合材料 ,  分子鎖 ,  *その場重合 ,  単量体
準シソーラス用語： 固有粘度 ,  溶融粘度 ,  LOI【酸素】 , 【Automatic Indexing@JST】

著者キーワード (4件)： P-glass ,  flame retardant copolyester ,  anti-dripping ,  nanocomposite

分類 (1件)： 抵抗性  (YH02050K)

タイトルに関連する用語 (5件)： その場重合 ,  ポリエステル ,  リン酸塩ガラス ,  複合材料 ,  研究