CO_3O_4ナノ粒子の吸着と吸着特性に及ぼす熱処理温度の影響を研究した。【JST・京大機械翻訳】

Effect of Calcination Temperature on Gas-Sensing and Adsorption Performance of Co_3O_4 Nanosheets from Solvothermal Synthesis

著者 (5件)： Li Xiaoting (School of Materials Science and Engineering, Tianjin University of Technology) ,  Zhang Lexi (School of Materials Science and Engineering, Tianjin University of Technology, Tianjin Key Lab for Photoelectric Materials and Devices) ,  Yin Jing (School of Environmental Science and Safety Engineering, Tianjin University of Technology) ,  Zhao Lixin (School of Environmental Science and Safety Engineering, Tianjin University of Technology) ,  Bie Lijian (School of Materials Science and Engineering, Tianjin University of Technology, Tianjin Key Lab for Photoelectric Materials and Devices)
資料名： Wuji Huaxue Xuebao  (Wuji Huaxue Xuebao)
巻： 32  号： 10  ページ： 1739-1746  発行年： 2016年 
JST資料番号： C2431A  ISSN： 1001-4861  CODEN： WHUXEO  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 開始剤としてCO(AC)_2 4H_2Oと6(HMTA)を用い,界面活性剤としてポリオキシエチレン-ポリオキシプロピレン-ポリエチレンオキシド(P123)を用いて,エチレングリコール(EG)と水混合溶媒中でソルボサーマル法により中間体を得た。CO_3O_4ナノシートをか焼により調製した。XRD,SEM,およびN_2吸着-脱着を用いて,生成物のモルフォロジーと結晶度に及ぼす種々の熱処理温度の影響を研究し,そして,備納米片のガス検知特性を研究した。ガス検知と吸着の結果に基づき,ガス検知機構と吸着動力学を分析した。結果は以下を示す。熱処理温度は生成物のモルフォロジーに影響する主要因であり,350°Cは最適熱処理温度であり,そのときに得られたナノシートは最も均一であった。生成物の形態変化は材料の比表面積を変化させ,生成物のガス検知性能と吸着性能に影響する。全体としてナノシートの厚さが小さいほど比表面積が大きくなり,材料のガス検知感度と吸着効率が高くなる。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： か焼 ,  モルフォロジー ,  比表面積 ,  X線回折 ,  重合開始剤 ,  結晶度 ,  *ナノ粒子 ,  *吸着 ,  ナノシート ,  ガス検知 ,  ソルボサーマル合成 ,  混合溶媒 ,  *熱処理温度 ,  *吸着特性
準シソーラス用語： 吸着動力学 , 【Automatic Indexing@JST】

著者キーワード (5件)： cobaltosic oxide ,  nanosheets ,  solvothermal synthesis ,  gas sensing ,  adsorption