Dai Jingjie について
Suzhou Institute, Shandong University, Suzhou 215123, Jiangsu, PR China について
Dai Jingjie について
Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, School of Materials Science and Engineering, Shandong University, Ji’nan 250061, Shandong, PR China について
Dai Jingjie について
Qingdao Binhai University, Qingdao 266555, Shandong, PR China について
Zhang Fengyun について
Qingdao Binhai University, Qingdao 266555, Shandong, PR China について
Wang Amin について
Qingdao Binhai University, Qingdao 266555, Shandong, PR China について
Yu Huijun について
Suzhou Institute, Shandong University, Suzhou 215123, Jiangsu, PR China について
Yu Huijun について
Key Laboratory of High-efficiency and Clean Mechanical Manufacture (Shandong University), Ministry of Education, School of Mechanical Engineering, Shandong University, Ji’nan 250061, Shandong, PR China について
Chen Chuanzhong について
Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, School of Materials Science and Engineering, Shandong University, Ji’nan 250061, Shandong, PR China について
Surface & Coatings Technology について
硬度 について
被覆 について
表面性状 について
高温酸化 について
高温 について
被覆層 について
耐酸化性 について
ケイ素 について
アルミニウム について
チタン について
レーザ表面合金化 について
亀裂 について
チタン合金 について
貫通亀裂 について
酸化挙動 について
Ti-6Al-4V について
レーザ表面合金化 について
Ti-Al-Siコーティング について
高温耐酸化性 について
金属材料へのセラミック被覆 について
レーザ表面合金化 について
作製 について
Ti について
Al について
Si について
被覆層 について
微細構造 について
性質 について