超臨界CO_2によって誘起されたポリカーボネートの結晶化の分子量依存性【Powered by NICT】

Molecular weight dependence of the crystallization of the polycarbonate induced by supercritical CO₂

著者 (5件)： Sun Ying (Department of Chemical Engineering, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima 739-8527, Japan) ,  Matsumoto Miki (Department of Chemical Engineering, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima 739-8527, Japan) ,  Haruki Masashi (Department of Chemical Engineering, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima 739-8527, Japan) ,  Kihara Shin-ichi (Department of Chemical Engineering, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima 739-8527, Japan) ,  Takishima Shigeki (Department of Chemical Engineering, Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima 739-8527, Japan)
資料名： Journal of Supercritical Fluids  (Journal of Supercritical Fluids)
巻： 113  ページ： 144-149  発行年： 2016年07月 
JST資料番号： W1591A  ISSN： 0896-8446  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 超臨界CO_2存在下でのポリカーボネート(PC)の結晶度と結晶化速度に及ぼす分子量の影響を,75から175°Cまで,そして20MPaまでの圧力で温度で研究した。結晶度は約0.05を減少させ,最大結晶化速度は19.2~29.8kg/molからPCの重量平均分子量の増加に伴って約50%減少した。さらに,最大結晶化速度は適切にガラス転移温度と融解温度溶解CO_2の可塑化効果により引き起こされる変化を考慮して30%の平均絶対誤差で相関していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶度 ,  ガラス転移点 ,  *ポリカーボネート ,  晶析速度 ,  融点 ,  *結晶化 ,  *分子量 ,  溶解 ,  *超臨界 ,  可塑化 ,  超臨界二酸化炭素
準シソーラス用語： 絶対誤差 ,  重量平均分子量 ,  *分子量依存性 , 【Automatic Indexing@JST】

著者キーワード (3件)： 結晶化 ,  ポリカーボネート ,  超臨界二酸化炭素

分類 (2件)： 薬物の物理化学的性質  (GV01060M) ,  分子化合物  (CE02000C)

タイトルに関連する用語 (5件)： 超臨界 ,  誘起 ,  ポリカーボネート ,  結晶化 ,  分子量依存性