コロナ放電におけるポリイミド/アルミナ複合膜の老化過程と破壊特性を研究した。【JST・京大機械翻訳】

Aging Process and Breakdown Characteristic of Polyimide/Al_2O_3 Composite Film Under Corona Discharge

著者 (6件)： Zhang Mingyu (School of Materials Science and Engineering, Harbin University of Science and Technology) ,  Liu Lizhu (School of Materials Science and Engineering, Harbin University of Science and Technology, Key Laboratory of Engineering Dielectric and Its Application of Ministry of Education) ,  Weng Ling (School of Materials Science and Engineering, Harbin University of Science and Technology) ,  Cui Weiwei (School of Materials Science and Engineering, Harbin University of Science and Technology) ,  Tian Feng (School of Materials Science and Engineering, Harbin University of Science and Technology) ,  Wang Cheng (School of Materials Science and Engineering, Harbin University of Science and Technology)
資料名： Gaodianya Jishu  (Gaodianya Jishu)
巻： 42  号： 12  ページ： 3941-3947  発行年： 2016年 
JST資料番号： C2121A  ISSN： 1003-6520  CODEN： GAJIE5  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： コロナ放電による複合膜絶縁の損傷過程を検討するために,GB/T22689-2008の基準を参照した。走査型電子顕微鏡(SEM),エネルギー分散型分光計(EDS),赤外分光法(FTIR)を用いて,コロナ放電によるPI/AL_2O_3薄膜の劣化を研究した。実験結果は以下を示す。コロナ放電時間の延長に伴い,コロナ破壊面の表面が破壊され,表面の有機物が徐々に減少し,アルミナが増加し,酸化アルミニウムの表面が連続的に被覆層を形成した。コロナ老化破壊後に形成された撃穿孔は20ΜM程度の円形ホールであり、位置の位置を位置、コロナ放電が破壊されない領域内に位置し、中心では放熱しにくい領域で、コロナ老化破壊は従来の電気絶縁破壊と電気化学的破壊によるものではないことを示している。しかしコロナ放電による熱蓄積により材料が発生した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 分光計 ,  *アルミナ ,  蓄熱 ,  破面 ,  穿孔 ,  *複合膜 ,  走査電子顕微鏡 ,  絶縁破壊 ,  酸化アルミニウム ,  エネルギー散逸 ,  *コロナ放電 ,  電気化学 ,  *太陽コロナ ,  被覆層
準シソーラス用語： 破壊特性 , 【Automatic Indexing@JST】

著者キーワード (6件)： polyimide ,  PI/Al_2O_3 composite film ,  corona discharge ,  aging ,  heat accumulation ,  breakdown