低炭素鋼のミクロ組織と特性に及ぼすI&Q&Pの影響を研究した。【JST・京大機械翻訳】

Effect of dual-phase region partitioning temperature on microstructure and properties of low carbon steel containing copper by I&Q&P process

著者 (6件)： Chen Liansheng (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Mi Zhenpeng (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Tian Yaqiang (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Zheng Xiaoping (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Song Jinying (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Xu Jinghui (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology)
資料名： Jinshu Rechuli  (Jinshu Rechuli)
巻： 41  号： 10  ページ： 162-166  発行年： 2016年 
JST資料番号： C2061A  ISSN： 0254-6051  CODEN： JRECDB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 0.12C-1.33MN-0.55CU鋼の微細構造と残留オーステナイト含有量に及ぼす二合金元素の異なる分配温度の影響を,走査型電子顕微鏡,X線回折,および電子プローブを用いて研究した。結果は以下を示す。試験結果は,C,CU,およびMN元素の分布が,二の分配の後に,明らかに,CU,MN元素の分配が,塩類の分級のためのCの組成を促進し,より多くの残留オーステナイトを保持することができることを示した。I&Q&Pプロセスにより,マルテンサイトと残留オーステナイトが得られ,二の分布温度が増加すると,オーステナイト粒のサイズが大きくなり,マルテンサイトのサイズが増加し,結晶粒度が増加した。分布温度の上昇とともに,引張強さは増加し,伸びは減少し,残留オーステナイト含有量の変化傾向は,伸び率と基本的に一致し,そして,残留オーステナイトの体積分率および伸びは,それぞれ,14.7%および24.4%であった。総合的機械的性質は最良であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 結晶粒度 ,  合金元素 ,  体積率 ,  分級 ,  *鋼 ,  引張強さ ,  走査電子顕微鏡 ,  マルテンサイト ,  伸び ,  X線回折 ,  オーステナイト ,  残留オーステナイト ,  伸び率 ,  電子プローブ ,  *低炭素鋼

著者キーワード (5件)： I&Q&P process ,  dual-phase region ,  partitioning temperature ,  mechanical properties ,  retained austenite

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (3件)： 低炭素鋼 ,  ミクロ組織 ,  研究