Sb_2O_3Na_2O WO_3PbO系内の新しい重金属酸化物ガラスの結晶化速度論【Powered by NICT】

Crystallization kinetics of new heavy metal oxide glasses within the Sb₂O₃-Na₂O-WO₃-PbO system

著者 (4件)： Ersundu M. Celikbilek (Yildiz Technical University, Department of Metallurgical and Materials Engineering, Faculty of Chemical and Metallurgical Engineering, Istanbul, 34220, Turkey) ,  Ersundu A.E. (Yildiz Technical University, Department of Metallurgical and Materials Engineering, Faculty of Chemical and Metallurgical Engineering, Istanbul, 34220, Turkey) ,  Soltani M.T. (University of Biskra, Laboratory of Physics of Photonics and Multifunctional Nanomaterials, BP 145, RP, 07000 Biskra, Algeria) ,  Baazouzi M. (University of Biskra, Laboratory of Physics of Photonics and Multifunctional Nanomaterials, BP 145, RP, 07000 Biskra, Algeria)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 1 PA  ページ： 491-497  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Sb_2O_3Na_2O WO_3PbO系内の新しい四元アンチモナイトガラスの結晶化速度論的研究を,示差走査熱量測定(DSC),X線回折(XRD)と走査電子顕微鏡(SEM)法を用いて非等温法により行った。ガラスにおける結晶化反応機構を決定する速度論パラメータnとmは結晶化した体積分率,χの実験値を用いて得られた,Ozawa法を適用した。nとmの値は1SEM研究によって確認された表面結晶化を示しているであることが分かった。結晶化活性化エネルギーの値は,七つの異なる理論的モデルを用いて234 272kJ/molの範囲で計算した。計算した結晶化の活性化エネルギー値はSb_2O_3の立方晶結晶方安鉱相の結晶化と関連していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *結晶 ,  走査電子顕微鏡 ,  体積率 ,  *晶析速度 ,  *ガラス ,  活性化エネルギー ,  示差走査熱量測定 ,  *結晶化 ,  *重金属 ,  X線回折 ,  反応機構
準シソーラス用語： 理論モデル ,  *酸化物ガラス , 【Automatic Indexing@JST】

著者キーワード (4件)： 重金属酸化物ガラス ,  Senarmontite ,  結晶化速度論 ,  非等温法

分類 (4件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G) ,  ガラスの製造  (YC02020O) ,  二次電池  (YB04030K)

タイトルに関連する用語 (3件)： 重金属 ,  酸化物ガラス ,  結晶化速度論