鋳鉄の乾式加工の間のダイヤモンドの摩耗機構を研究した。【JST・京大機械翻訳】

Wear mechanism of brazed diamond saws during dry-cutting cast iron

著者 (4件)： Liu Sixing (Jiangsu Key Laboratory of Precision and Micro-manufacturing Technology, College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics) ,  Xiao Bing (Jiangsu Key Laboratory of Precision and Micro-manufacturing Technology, College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics) ,  Zhang Ziyu (Jiangsu Key Laboratory of Precision and Micro-manufacturing Technology, College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics) ,  Chen Yuguo (Jiangsu Key Laboratory of Precision and Micro-manufacturing Technology, College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics)
資料名： Zhongguo Youse Jinshu Xuebao  (Zhongguo Youse Jinshu Xuebao)
巻： 26  号： 10  ページ： 2166-2173  発行年： 2016年 
JST資料番号： W0943A  ISSN： 1004-0609  CODEN： ZYJXFK  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： NI-CR合金の活性はんだを用いて,高真空炉でダイヤモンドと鋼基材の間の強固な接着を実現した。走査型電子顕微鏡(SEM),エネルギー分散分光法(EDS),X線回折(XRD)を用いて,真空ろう付ダイヤモンドのろう付機構と界面特性を説明し,乾式加工鋳鉄の摩耗特性を分析した。結果は以下を示す。鋳鉄管の加工において,ろう付ダイヤモンドは,高効率の切断性能を示し,そして,研磨摩耗は,主に破砕を主とし,そして,研削温度は,研磨面の表面に付着した。鋳鉄の乾式加工の間,ダイヤモンドの摩耗表面には,黒鉛化摩耗のようないくつかの現象があることがわかった。実験結果は,研磨剤の強度が加工の必要条件を満たすことができることを示した。鋳鉄材料の高効率加工のために,高強度,高強度,および安全性を有するダイヤモンド状炭素鋼を開発した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： アブレシブ摩耗 ,  X線回折 ,  ダイヤモンド状炭素 ,  黒鉛化 ,  摩耗特性 ,  *鋳鉄 ,  真空ろう付 ,  *摩耗 ,  走査電子顕微鏡 ,  ろう付 ,  はんだ ,  研磨剤 ,  *ダイヤモンド
準シソーラス用語： 高強度 ,  *摩耗機構 , 【Automatic Indexing@JST】

著者キーワード (5件)： diamond saws ,  cast iron pipe ,  vacuum brazing ,  wear mechanism ,  dry-cutting

分類 (3件)： 炭素とその化合物  (YB02060D) ,  機械的性質  (WB02030U) ,  その他の無機化合物の薄膜  (BK14060A)

タイトルに関連する用語 (5件)： 鋳鉄 ,  乾式加工 ,  ダイヤモンド ,  摩耗 ,  研究