音波IRイメージングを用いた金属板の厚さによる疲労き裂の加熱特性【Powered by NICT】

Heating characterization of the thickness-through fatigue crack in metal plate using sonic IR imaging

著者 (7件)： Feng Fu-zhou (Key laboratory of Nondestructive Testing, Ministry of Education, Nanchang, China) ,  Feng Fu-zhou (Department of Mechanical Engineering, Academy of Armored Forces Engineering, Beijing, China) ,  Zhang Chao-sheng (Engineer Academy of PLA, Xuzhou, China) ,  Min Qing-xu (Department of Mechanical Engineering, Academy of Armored Forces Engineering, Beijing, China) ,  Zhu Jun-zhen (Department of Mechanical Engineering, Academy of Armored Forces Engineering, Beijing, China) ,  Wang Wei-jie (Peking University, Beijing, China) ,  Chao Xu (Department of Mechanical Engineering, Academy of Armored Forces Engineering, Beijing, China)
資料名： NDT & E International  (NDT & E International)
巻： 87  ページ： 38-43  発行年： 2017年 
JST資料番号： A0196A  ISSN： 0963-8695  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 音波IRイメージングでは,主要な問題は,試験条件の最適化を導くために亀裂近傍の加熱特性を調べた。本論文では,人工疲労亀裂を有する金属板の亀裂の加熱特性を調べた。実験結果は,超音波励起中の板の励起側で亀裂近傍の温度上昇はその反対側のそれよりも高いことを示したが,亀裂面の全加熱効率は安定であると思われる。亀裂面のプロファイルマッピングにより,摩擦加熱は主に励起側に集中している。この現象に基づいて,亀裂近傍の温度分布を計算する数学的熱伝達モデルを構築し,亀裂面の加熱特性を調べた。,数学モデルは前面でのそれと反対側に熱源の深さと亀裂近傍の温度分布の比との間の定量的関係を与えた。音波IRイメージングにおける摩擦加熱領域の位置決定のための定量的評価法を提供することを目的とする。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 数学モデル ,  亀裂 ,  *金属板 ,  熱源 ,  超音波 ,  温度分布 ,  *疲れ亀裂 ,  位置決め ,  励起 ,  *音波 ,  最適化 ,  昇温 ,  *画像処理
準シソーラス用語： 定量的評価 ,  摩擦加熱 , 【Automatic Indexing@JST】

著者キーワード (5件)： 音波IRイメージング ,  金属板 ,  厚さを通して疲労き裂 ,  亀裂加熱 ,  伝熱モデル

分類 (1件)： 非破壊試験  (HB02030F)

タイトルに関連する用語 (6件)： 音波 ,  Ir ,  イメージング ,  金属板 ,  厚さ ,  疲労き裂