アルミニウム電解酸化チタン被覆酸化防止塗料の研究【JST・京大機械翻訳】

Study on protective coating with anti-oxidation for carbon anodes in aluminum electrolysis

著者 (6件)： Li Ling (State Key Laboratory of Light Alloy Casting Technology for High-end Equipment,Shenyang Research Institute of Foundry) ,  Yin Shaokui (State Key Laboratory of Light Alloy Casting Technology for High-end Equipment,Shenyang Research Institute of Foundry) ,  Gao Tianjiao (State Key Laboratory of Light Alloy Casting Technology for High-end Equipment,Shenyang Research Institute of Foundry) ,  Huang Danzhong (State Key Laboratory of Light Alloy Casting Technology for High-end Equipment,Shenyang Research Institute of Foundry) ,  Liu Jiajun (State Key Laboratory of Light Alloy Casting Technology for High-end Equipment,Shenyang Research Institute of Foundry) ,  Li Yanhai (State Key Laboratory of Light Alloy Casting Technology for High-end Equipment,Shenyang Research Institute of Foundry)
資料名： Qingjinshu  (Qingjinshu)
号： 11  ページ： 38-41  発行年： 2016年 
JST資料番号： C2967A  ISSN： 1002-1752  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 本論文では,アルミニウムの電解酸化防止コーティングを紹介し,コーティングの高温酸化抵抗と耐食性に及ぼす複合酸化防止剤と腐食防止剤の影響を研究した。実験結果は,アルミニウム合金とホウ化物が,高温での被覆の緻密化に重要な役割を果たすことを示し,それは,コーティングの高温緻密性を大いに改善し,高温酸化抵抗を向上させることができる。しかし,フッ化物の添加は,コーティングの高温耐食性を改善し,アルミニウムの電解プロセスにおけるコーティングの腐食を軽減した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 耐食性 ,  ホウ化物 ,  *アノード酸化 ,  *電解 ,  酸化防止剤 ,  高温 ,  *被覆 ,  腐食抑制剤 ,  緻密化 ,  高温酸化 ,  *酸化防止 ,  アルミニウム合金 ,  *アルミニウム ,  フッ化物
準シソーラス用語： *アルミニウム電解 , 【Automatic Indexing@JST】

著者キーワード (4件)： carbon anode ,  anti-oxidation ,  anti-corrosion ,  coating compactness