1673KにおけるC_f/SiC複合材料のためのプラズマ溶射Si/Yb_2Si_2O_7/LaMgAl_11O_19皮膜の作製と耐酸化性挙動【Powered by NICT】

Fabrication and oxidation resistant behavior of plasma sprayed Si/Yb₂Si₂O₇/LaMgAl₁₁O₁₉ coating for C_f/SiC composites at 1673K

著者 (12件)： Fan Wenjuan (Hunan Provincial Key Laboratory of Materials Protection for Electric Power and Transportation, School of Chemistry and Biological Engineering, Changsha University of Science and Technology, Changsha 410114, Hunan, China) ,  Fan Wenjuan (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, Jilin, China) ,  Zou Binglin (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, Jilin, China) ,  Fan Cunyan (Hunan Provincial Key Laboratory of Materials Protection for Electric Power and Transportation, School of Chemistry and Biological Engineering, Changsha University of Science and Technology, Changsha 410114, Hunan, China) ,  Fan Cunyan (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, Jilin, China) ,  Wang Ying (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, Jilin, China) ,  Cai Xiaolong (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, Jilin, China) ,  Tao Shunyan (Key Laboratory of Inorganic Coating Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Xu Jiaying (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, Jilin, China) ,  Wang Chunjie (State Key Laboratory of Rare Earth Resources Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, Jilin, China) ,  Cao Xueqiang (State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, Hubei, China) ,  Zhu Ling (Hunan Provincial Key Laboratory of Materials Protection for Electric Power and Transportation, School of Chemistry and Biological Engineering, Changsha University of Science and Technology, Changsha 410114, Hunan, China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 1 PA  ページ： 392-398  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： C_f/SiC複合材料をSi結合層のないYb_2Si_2O_7/LaMgAl_11O_19被覆をプラズマ溶射した。1673Kでの被覆の微細構造と酸化保護を調べた。結果によると,皮膜は粉体のそれと同じ相組成を持ち,基板上に均一に分布することを示した。Si結合層をもつ皮膜と基材の間の接合界面はSiなし結合層のそれよりも良好であった。1673Kで90分間の加熱の15サイクル後,Si結合層無しの被覆試料の重量損失は2.54%と21.89%であったが,非被覆試料の重量損失は36.47%であった。ある程度まで,Si結合層は基板の表面上に多孔性を治癒し効率的に,被覆と基板の間の熱膨張係数(CTE)のミスマッチを軽減し,被覆の酸化保護を有意に改善した。C_f/SiC複合材料内の皮膜と基板の間のCTE,LaMgAl_11O_19とYb_2Si_2O_7層の間の化学反応と正孔と亀裂の差は被覆の耐酸化性に不利であった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 重量損失 ,  *ケイ素 ,  *プラズマ溶射 ,  多孔性 ,  被覆 ,  正孔 ,  相組成 ,  *皮膜 ,  熱膨張係数 ,  *炭化ケイ素 ,  *耐酸化性 ,  不整合 ,  *複合材料
準シソーラス用語： 接合界面 ,  酸化保護 , 【Automatic Indexing@JST】

著者キーワード (4件)： C_f/SiC複合材料 ,  塗料 ,  耐酸化性 ,  プラズマ溶射

分類 (1件)： 非金属材料へのセラミック被覆  (YC02040K)