Growth and Thermo-luminescence Properties of Dy: Bi_4Si_3O_(12) Crystals

著者 (7件)： Wang Meiling (School of Materials Science and Engineering, Shanghai Institute of Technology) ,  Xu Jiayue (School of Materials Science and Engineering, Shanghai Institute of Technology) ,  Zhang Yan (School of Materials Science and Engineering, Shanghai Institute of Technology) ,  Chu Yaoqing (School of Materials Science and Engineering, Shanghai Institute of Technology) ,  Yang Bobo (School of Materials Science and Engineering, Shanghai Institute of Technology) ,  Shen Hui (School of Materials Science and Engineering, Shanghai Institute of Technology) ,  Tian Tian (School of Materials Science and Engineering, Shanghai Institute of Technology)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 31  号： 10  ページ： 1068-1072  発行年： 2016年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 0.1MOL%,0.2MOL%,0.3MOL%,2MOL%,3MOL%,および4MOL%のBI_4SI_3O_(12)(BSO)結晶を,るつぼ法によって成長させた。その結果,高濃度(2MOL%以上)のドーピングは,結晶の結晶化挙動を著しく変化させ,結晶表面の析出物は完全に消失し,そして,頂部は滑らかな結晶面を示した。低濃度(0.3MOL%以下)のドーピングは,結晶の光出力を著しく増加させ,純BSOの最大値に達することができた。結晶の熱ルミネセンススペクトルは,以下のことを示した。少量のDY(3+)のドーピングは,ピークをわずかに増強したが,結晶収率の増加に有利であった。高濃度ドーピングは格子歪を起こしやすく,新しい欠陥を生じ,結晶の光収率を低下させる。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 格子歪 ,  *熱ルミネセンス ,  坩堝 ,  析出物 ,  *ドーピング ,  発光スペクトル ,  結晶面 ,  *結晶
準シソーラス用語： 光出力 ,  低濃度 ,  結晶表面 ,  結晶化挙動 ,  高濃度 , 【Automatic Indexing@JST】

著者キーワード (5件)： Bi_4Si_3O_(12) ,  crystal growth ,  Dy(3+) doping ,  thermoluminescence ,  light yield