高温酸化後のTI6AL4V合金の微細構造と機械的性質を調べた。【JST・京大機械翻訳】

Microstructure and Mechanical Properties of Oxygen-Diffusion Layer on Ti6Al4VAlloy after High-Temperature Oxidation

著者 (5件)： Pan Renjing (Key Laboratory of Pressure Systems and Safety,Department of Mechanical Engineering, East China University of Science and Technology) ,  Zhang Yang (Key Laboratory of Pressure Systems and Safety,Department of Mechanical Engineering, East China University of Science and Technology) ,  Zhang Xiancheng (Key Laboratory of Pressure Systems and Safety,Department of Mechanical Engineering, East China University of Science and Technology) ,  Tu Shantung (Key Laboratory of Pressure Systems and Safety,Department of Mechanical Engineering, East China University of Science and Technology) ,  Qian Xiayi (Special Equipment Safety Supervision Inspection Institute of Jiangsu Province)
資料名： Jixie Gongcheng Cailiao  (Jixie Gongcheng Cailiao)
巻： 40  号： 11  ページ： 71-74,97  発行年： 2016年 
JST資料番号： C2051A  ISSN： 1000-3738  CODEN： JGCAEL  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 850°CでTI6AL4V(TC4)チタン合金板をそれぞれ12,24,36,48Hの酸化処理を行い,高温酸化処理後の合金表面の微細構造と機械的性質を研究した。結果は以下を示す。高温酸化後のチタン合金の表面層にはShenYang層が出現し、それは間原子の固溶によって形成され、ShenYang層中の酸素含有量は勾配分布を呈する。深さの増加とともに,ShenYang層の硬度,弾性率および残留引張応力は,徐々に減少した。格子定数の変化は,酸素原子のマトリックス中で起こり,それは,傾斜構造の形成と機械的性質の増加のための主な理由であった。残留応力の変化は酸化過程における酸素拡散と空冷過程における熱応力の共同作用の結果である。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *合金 ,  空気冷却 ,  *機械的性質 ,  残留応力 ,  表層 ,  熱応力 ,  引張応力 ,  チタン合金 ,  *酸化 ,  *高温酸化 ,  協力作用 ,  格子定数 ,  硬度
準シソーラス用語： 酸素拡散 ,  酸化処理 , 【Automatic Indexing@JST】

著者キーワード (6件)： Ti6Al4V alloy ,  oxygen-diffusion layer ,  elasticity modulus ,  mechanical property ,  lattice parameter ,  residual stress

分類 (6件)： 金属材料へのセラミック被覆  (YC02050V) ,  溶射  (WC08030N) ,  その他の表面処理  (WC08070F) ,  金属材料  (HC05020S) ,  表面硬化熱処理  (WC03030E) ,  金属の機械的性質  (BL01022T)

タイトルに関連する用語 (3件)： 高温酸化 ,  微細構造 ,  機械的性質