Preparation and Graphene Modification of Nano Perovskite La_(1-x)Sr_xMnO_3

著者 (8件)： Lu Weizhong (College of Chemical and Environmental Engineering,Shenzhen University) ,  Wang Yake (College of Chemical and Environmental Engineering,Shenzhen University) ,  Qiu Qi (College of Chemical and Environmental Engineering,Shenzhen University) ,  Ruan Wenke (College of Chemical and Environmental Engineering,Shenzhen University) ,  Zhou Xiaochu (College of Chemical and Environmental Engineering,Shenzhen University) ,  Zheng Weimeng (College of Chemical and Environmental Engineering,Shenzhen University) ,  Ji Shan (College of Chemical and Environmental Engineering,Shenzhen University) ,  Zhang Dongping (College of Physics and Energy,Shenzhen University)
資料名： Jingxi Huagong  (Jingxi Huagong)
巻： 33  号： 12  ページ： 1339-1343,1421  発行年： 2016年 
JST資料番号： W1078A  ISSN： 1003-5214  CODEN： JIHUFJ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： LA_(1-X)SR_XMNO_3(X=0,0.1,0.2,0.3,0.4,0.5)を超音波支援ゾル-ゲル法によって調製し,それらをグラフェンのドーピングによって修飾した。LA_(1-X)SR_XMNO_3とグラフェン/LA_(1-X)SR_XMNO_3複合材料の構造を,XRD,SEM-EDS,およびDLSによって特性評価した。LA_(1-X)SR_XMNO_3の結晶相とサイズに及ぼすか焼温度とPH値の影響を研究し,複合材料の性質に及ぼすグラファイトの影響を試験した。結果は以下を示す。超音波支援条件下で,650°C,PH=10で調製したLA_(1-X)SR_XMNO_3は,良好な分散性を示し,平均粒径は210NMであった。XRD結果は以下を示す。グラフェンドーピングは,LA_(1-X)SR_XMNO_3結晶相を変化させなかった。最初の充放電実験結果は以下のことを示した。ウールと比較して,グラフェンドーピングで修飾した複合材料は触媒としてのリチウム空気電池で,初回放電容量は4MAH/Gから7MAH/Gに増加した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： キャラクタリゼーション ,  分散度 ,  ゾル-ゲル法 ,  羊毛 ,  超音波 ,  X線回折 ,  複合材料 ,  グラファイト ,  *グラフェン
準シソーラス用語： 放電容量 ,  リチウム-空気電池 ,  充放電 ,  平均粒子径 ,  か焼温度 ,  結晶相 , 【Automatic Indexing@JST】

著者キーワード (4件)： perovskite ,  graphene ,  doping modified ,  functional materials