表面の機械的アトリション処理により誘起された純鉄中のけい素化挙動の増強【Powered by NICT】

Enhancement of siliconizing behaviors in pure iron induced by surface mechanical attrition treatment

著者 (6件)： Li Yang (College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024, PR China) ,  Hou Lifeng (College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024, PR China) ,  Wei Yinghui (College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024, PR China) ,  Wei Yinghui (Shanxi Institute of Technology, Yangquan, Shanxi 045000, PR China) ,  Wei Huan (College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024, PR China) ,  Cheng Yang (College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024, PR China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 309  ページ： 462-470  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 厚さ約100μmの勾配ナノ構造表面層が表面機械的摩耗処理(SMAT)により誘起された純鉄上に合成した。上面における平均粒径は約20nmであった。Fe-Si化合物層の形成挙動を無電解ケイ素化プロセス中のナノ構造化Feで検討した。粗粒(CG)試料と比較して,SMAT試料上の化合物層の厚さはCG試料よりも約2倍大きく,拡散活性化エネルギーはSMAT20分後の試料の231kJ/mol molに減少した。FeとSiのような元素の明白な相互拡散はEDS分析下で認められ,金属学的な結合の達成を示唆した。空隙率はKirkendall効果によるCG試料中のマトリックスとFe_3Si層の界面に現れたが,化合物層とマトリックスの結合はSMAT試料中の元素拡散の促進によりtighterであった。強化されたけい素動力学はナノ構造化表面と変形層における多数の粒界(GB)に起因した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *鉄 ,  ナノ構造 ,  Kirkendall効果 ,  電解 ,  相互拡散 ,  表層 ,  界面 ,  *ケイ素 ,  金属工学 ,  結晶粒界 ,  活性化エネルギー ,  *純鉄 ,  空隙率
準シソーラス用語： 機械的摩耗表面処理 , 【Automatic Indexing@JST】

著者キーワード (5件)： 表面機械的アトリション処理 ,  けい化処理 ,  反応拡散 ,  成長速度論 ,  Fe_3Si化合物

分類 (3件)： 防食  (WB03040M) ,  肉盛  (WC07060N) ,  金属材料へのセラミック被覆  (YC02050V)

タイトルに関連する用語 (5件)： 誘起 ,  純鉄 ,  けい素 ,  挙動 ,  増強