Investigation on Yb(3+)-doped silica glass using sol-gel method and laser melting technology

著者 (7件)： Liang Wanting (Guangzhou Key Laboratory for Special Fiber Photonic Devices and Applications, South China Normal University) ,  Hou Zhiyun (Guangzhou Key Laboratory for Special Fiber Photonic Devices and Applications, South China Normal University) ,  Zhou Guiyao (Guangzhou Key Laboratory for Special Fiber Photonic Devices and Applications, South China Normal University) ,  Xia Changming (Guangzhou Key Laboratory for Special Fiber Photonic Devices and Applications, South China Normal University) ,  Zhang Wei (Guangzhou Key Laboratory for Special Fiber Photonic Devices and Applications, South China Normal University) ,  Wei Lefeng (Guangzhou Key Laboratory for Special Fiber Photonic Devices and Applications, South China Normal University) ,  Liu Jiantao (Guangzhou Key Laboratory for Special Fiber Photonic Devices and Applications, South China Normal University)
資料名： Wuli Xuebao  (Wuli Xuebao)
巻： 65  号： 17  ページ： 178107-01-178107-05  発行年： 2016年 
JST資料番号： B0628A  ISSN： 1000-3290  CODEN： WLHPA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： CanYi石英基ガラスは,高出力ファイバレーザのための利得ファイバを研究するためのコア材料である。本論文では,前駆体としてTEOS,ALCL_3,YBCL_36H_2Oを用いるゾル-ゲル法により,石英粉末を調製し,レーザ焼結技術により,石英ガラスを調製した。実験結果は以下を示す。高温処理時の合理的な温度制度を制御することにより、乾燥ゲルの水分と有機物を有効に排除でき、調製したガラスサンプルは結晶化現象がなく、良好な光学特性を示した。これらの実験結果は,将来の引の光ファイバドープファイバと,高出力レーザの開発において重要な役割を果たす。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *レーザ融解 ,  レーザ焼結 ,  ファイバレーザ ,  *石英ガラス ,  高出力レーザ ,  ゾル-ゲル法 ,  *ガラス ,  キセロゲル ,  利得 ,  *石英 ,  水分
準シソーラス用語： 高温処理 ,  コア材 ,  高出力 ,  *ゾル-ゲル , 【Automatic Indexing@JST】

著者キーワード (4件)： rare-earth-doped silica glass ,  Yb(3+)-doped ,  sol-gel method ,  laser melting