文献

J-GLOBAL ID：201702289946233141   整理番号：17A0162453

アルミニウム合金の溶接成形と機械的性質に及ぼす異なる溶接方法の影響を研究した。【JST・京大機械翻訳】

Study on the Influence of Different Welding Methods onAluminum Alloy Weld Formation and Mechanical Properties

著者 (6件)： Yang Xichang (School of Mechanical and Electrical Engineering,Changchun University of Science and Technology) ,  Liu Jia (School of Mechanical and Electrical Engineering,Changchun University of Science and Technology) ,  Zhang Jibin (School of Mechanical and Electrical Engineering,Changchun University of Science and Technology) ,  Shi Yan (School of Mechanical and Electrical Engineering,Changchun University of Science and Technology) ,  Jiang Shichun (School of Mechanical and Electrical Engineering,Changchun University of Science and Technology) ,  Li Hongxing (School of Mechanical and Electrical Engineering,Changchun University of Science and Technology)
資料名： Yingyong Jiguang  (Yingyong Jiguang)
巻： 36  号： 5  ページ： 553-558  発行年： 2016年 
JST資料番号： C2473A  ISSN： 1000-372X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 厚さ10MMの5083アルミニウム合金に対して,YAGレーザ溶接,溶融混合ガスアーク溶接(MIG)およびレーザ-MIGハイブリッド溶接試験を行い,3つの溶接線の成形,空隙率および微小硬さの差を比較した。3つの溶接方法によって得られた溶接部は,溶接において大きな差異があり,溶接金属の溶接において,溶接線の深さ,レーザ溶接線,MIG溶接線は,溶接部において最も大きかった。溶接幅に関しては,ハイブリッド溶接が最も大きく,MIGが最も小さく,レーザが最も小さかった。レーザは不安定性のため、プロセスの気孔を形成しやすく、空隙率が最も大きい。ハイブリッド溶接において,アークはプロセスの気孔を抑制するので,気孔率は小さい。3つの中でMIGが最も小さい。しかし,微小硬さに関しては,溶接線は溶接ワイヤを持たないMIG溶接の溶接線と比較して大きな差があり,レーザ溶接継手の硬度分布曲線は「V」形を示し,一方,MIG溶接線の硬度分布曲線は「W」形を示した。全体としてMIG溶接部の微小硬さが最も高い。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 溶接ワイヤ ,  気孔 ,  溶接線 ,  *溶接 ,  溶接継手 ,  溶接金属 ,  アーク放電 ,  空隙率 ,  MIG溶接 ,  微小硬さ ,  硬度 ,  レーザ溶接 ,  *アルミニウム合金
準シソーラス用語： 硬度分布 ,  ハイブリッド溶接 , 【Automatic Indexing@JST】

著者キーワード (6件)： aluminum alloy ,  laser welding ,  MIG welding ,  laser arc hybrid welding ,  porosity ,  microhardness

分類 (3件)： 溶接技術  (WC07030G) ,  溶接部  (WC07100I) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： アルミニウム合金 ,  溶接 ,  機械的性質 ,  研究