7A52厚板アルミニウム合金の摩擦撹拌溶接の性能を比較した。【JST・京大機械翻訳】

Properties of welded joints of 7A52 aluminum alloy thick-plate by single-side and double-side friction stir welding

著者 (7件)： Chen Donggao (School of Materials Science and Engineering,Northwestern Polytechnical University) ,  Liu Jinhe (School of Materials Science and Engineering,Northwestern Polytechnical University) ,  Chen Dongliang (Ningbo Branch of Chinese Academy of Ordnance Science) ,  Ma Zhihua (School of Materials Science and Engineering,Northwestern Polytechnical University) ,  Feng Shengqiang (School of Materials Science and Engineering,Northwestern Polytechnical University) ,  Yang Wulin (School of Materials Science and Engineering,Northwestern Polytechnical University) ,  Tao Mingjie (School of Materials Science and Engineering,Northwestern Polytechnical University)
資料名： Bingqi Cailiao Kexue yu Gongcheng  (Bingqi Cailiao Kexue yu Gongcheng)
巻： 39  号： 5  ページ： 29-31  発行年： 2016年 
JST資料番号： C2398A  ISSN： 1004-244X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 30MM厚さの7A52アルミニウム合金板の摩擦撹拌溶接試験を行い,溶接継手のミクロ組織と特性に及ぼす2つのプロセスの影響を比較した。結果は以下を示す。片面1溶接と比較して,両面(2回)の溶接は,1つの溶接部組織を微細化し,そして,溶接部の硬度を均一にし,そして,母材の硬度に達し,そして,溶接継手の伸びおよび引張強さは,単一溶接のそれより優れていた。両面溶接継手の破壊靭性は,破壊靭性を示し,一方,一つの溶接継手の破面の数は,両面のそれより低かった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *溶接 ,  伸び ,  *アルミニウム合金 ,  溶接部 ,  引張強さ ,  *摩擦撹拌溶接 ,  精密化 ,  破壊靱性 ,  溶接継手 ,  硬度 ,  *厚板 ,  破面 ,  機械的性質 ,  強度

著者キーワード (4件)： 7A52 aluminum alloy rolling plate ,  friction stir welding ,  second back welding ,  microstructure and property comparison