溶融の結晶形態,組成,および遷移層の性質に及ぼす溶融過冷却の影響を研究した。【JST・京大機械翻訳】

Effects of Undercooling Degree on the Morphology,Composition and Transition Layer of the Diopside Crystal

著者 (7件)： CHI Zhao-kun (Faculty of Materials Science and Chemical Engineering, China University of Geosciences) ,  TAN Jin (Faculty of Materials Science and Chemical Engineering, China University of Geosciences) ,  BAO Lu-ming (Faculty of Materials Science and Chemical Engineering, China University of Geosciences) ,  AI Fei (Faculty of Materials Science and Chemical Engineering, China University of Geosciences) ,  HUANG Yan-qiu (Faculty of Materials Science and Chemical Engineering, China University of Geosciences) ,  HE Mou-chun (Faculty of Materials Science and Chemical Engineering, China University of Geosciences) ,  LI Fei (Faculty of Materials Science and Chemical Engineering, China University of Geosciences)
資料名： Rengong Jingti Xuebao  (Rengong Jingti Xuebao)
巻： 38  号： 1  ページ： 88-94,106  発行年： 2009年 
JST資料番号： W0398A  ISSN： 1000-985X  CODEN： RJXUEN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 異なる過冷却条件の下で,ケイ酸塩メルトの結晶化により,透輝石結晶の適切な量のサンプルが得られた。実験結果によると、透過結晶の形態の自食度は過冷度の増加につれて低下する。RAMANスペクトル分析により、結晶の特徴スペクトルピークは過冷却度の増加により広くなり、ラマンスペクトルは結晶構造がガラス構造を継承する特徴を示した。電子プローブを用いて,透輝石結晶とその成長界面近くの組成変化の特徴を詳細に分析し,約十数ミクロンの厚さの遷移層が存在し,また,透過結晶の成分が過冷却度の増加に伴い,AL元素の結晶含有量も増加することが分かった。同時に,結晶化過程におけるAL元素とMG元素の間の相乗効果は,より強かった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 結晶構造 ,  *結晶形態 ,  ガラス構造 ,  結晶化 ,  相乗作用 ,  分光分析 ,  電子プローブ ,  *結晶 ,  Ramanスペクトル ,  *過冷却 ,  界面
準シソーラス用語： 組成変化 ,  サブクール度 ,  透輝石 ,  *遷移層 , 【Automatic Indexing@JST】

著者キーワード (5件)： diopside ,  crystallization ,  undercooling degrees ,  transition layer ,  crystal component

分類 (1件)： 岩石圏の地球化学一般  (DD01041C)

タイトルに関連する用語 (7件)： 溶融 ,  結晶形態 ,  組成 ,  遷移層 ,  性質 ,  過冷却 ,  研究