316LN型ステンレス鋼溶接継手の破壊靭性【Powered by NICT】

Fracture toughness of type 316LN stainless steel welded joints

著者 (4件)： Gao Wenhua (School of Nuclear Science and Engineering, Shanghai Jiao Tong University, No. 800 Dongchuan Road, Shanghai 200240, PR China) ,  Chen Kai (School of Nuclear Science and Engineering, Shanghai Jiao Tong University, No. 800 Dongchuan Road, Shanghai 200240, PR China) ,  Guo Xianglong (School of Nuclear Science and Engineering, Shanghai Jiao Tong University, No. 800 Dongchuan Road, Shanghai 200240, PR China) ,  Zhang Lefu (School of Nuclear Science and Engineering, Shanghai Jiao Tong University, No. 800 Dongchuan Road, Shanghai 200240, PR China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 685  ページ： 107-114  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 空気中300Kおよび623Kで種々の方位の二種類の316LN溶接継手の破壊靭性を調べた。試験は,単一試験片法を用いて行った,J-R曲線と破壊靭性値(J_0.2)を得た。試料のミクロ組織を試験前後に特性評価した。結果は2GT溶接継手は5GT溶接継手と比較して,より高い靭性を示し,配向が破壊靭性に及ぼすわずかな効果を持つことを示した。さらに,破壊靭性は温度の増加と共に著しく低下した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *靱性 ,  *破壊靱性 ,  ステンレス鋼 ,  キャラクタリゼーション ,  *溶接継手 ,  破壊靱性値 ,  *機械的性質

著者キーワード (4件)： 316LNステンレス鋼 ,  破壊靭性 ,  溶接継手 ,  Orientation

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (3件)： ステンレス鋼 ,  溶接継手 ,  破壊靭性