J-GLOBAL ID：201702297232104604   整理番号：17A0698443

Mg-Li合金の焼なまし時の析出過程【Powered by NICT】

Precipitation evolution during annealing of Mg-Li alloys

著者 (5件)： Tang Yan (Key Lab of Electromagnetic Processing of Materials, Ministry of Education, Northeastern University, Shenyang 110819, China) ,  Jia Weitao (Key Lab of Electromagnetic Processing of Materials, Ministry of Education, Northeastern University, Shenyang 110819, China) ,  Liu Xuan (Key Lab of Electromagnetic Processing of Materials, Ministry of Education, Northeastern University, Shenyang 110819, China) ,  Le Qichi (Key Lab of Electromagnetic Processing of Materials, Ministry of Education, Northeastern University, Shenyang 110819, China) ,  Cui Jianzhong (Key Lab of Electromagnetic Processing of Materials, Ministry of Education, Northeastern University, Shenyang 110819, China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 689  ページ： 332-344  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： α相とα+β相のミクロ組織進展及び機械的性質と熱処理後のβ相Mg-Li展伸合金を調べた。結果は,押出Mg5Li3Al2Zn 1.2Yでは,沈殿を220 320°Cの範囲12~時間では観察されなかったことを示した。押出Mg8Li3Al2Zn 1.2YとMg11Li3Al2Zn 1.2Y合金では,析出挙動は熱処理後にβ相中に生じた。しかし,押出したMg-11Li-1.2YとMg-11Li-3Al-0.2Ce合金では,降水量とβ相の固溶体の間の変換が存在した。添加では,合金の機械的性質は,降水量と固溶体によって著しく影響を受けた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 熱処理 ,  固溶体 ,  β相 ,  *合金 ,  沈殿 ,  *焼なまし ,  機械的性質 ,  降水量 ,  α相
準シソーラス用語： 微細構造進展 , 【Automatic Indexing@JST】

著者キーワード (5件)： 微細構造進化 ,  機械的性質 ,  熱処理 ,  沈殿 ,  固溶体

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： Mg-Li合金 ,  焼なまし ,  析出 ,  過程