広い温度範囲Mn_0 70Fe_0 25Cu_0 0.05合金の弾性率異常の起源【Powered by NICT】
Origin of the modulus anomaly over a wide temperature range of Mn0.70Fe0.25Cu0.05 alloy
著者 (9件):
Cui Yanguang
(UM-SJTU Joint Institute, Shanghai Jiaotong University, Dongchuan Road 800, Shanghai 200240, China)
,
Guo Yunlong
(UM-SJTU Joint Institute, Shanghai Jiaotong University, Dongchuan Road 800, Shanghai 200240, China)
,
Li Yangxin
(School of Material Science & Engineering, Shanghai JiaoTong University, Shanghai 200240, China)
,
Wan Jianfeng
(School of Material Science & Engineering, Shanghai JiaoTong University, Shanghai 200240, China)
,
Zhang Jihua
(School of Material Science & Engineering, Shanghai JiaoTong University, Shanghai 200240, China)
,
Rong Yonghua
(School of Material Science & Engineering, Shanghai JiaoTong University, Shanghai 200240, China)
,
Chen Nailu
(School of Material Science & Engineering, Shanghai JiaoTong University, Shanghai 200240, China)
,
Wang Dong
(Center for Computational Study of Microstructure Evolution in Materials and Multi-Disciplinary Materials Research Center, Frontier Institute of Science and Technology, State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China)
,
Wang Yunzhi
(Department of Materials Science and Engineering, The Ohio State University, 2041 College Road, Columbus, OH 43210, USA)
資料名:
Computational Materials Science
(Computational Materials Science)
巻:
140
ページ:
89-94
発行年:
2017年
JST資料番号:
W0443A
ISSN:
0927-0256
資料種別:
逐次刊行物 (A)
記事区分:
原著論文
発行国:
オランダ (NLD)
言語:
英語 (EN)