超臨界水中での新しいアルミナ形成オーステナイト系ステンレス鋼の腐食および応力腐食割れ挙動【Powered by NICT】
The corrosion and stress corrosion cracking behavior of a novel alumina-forming austenitic stainless steel in supercritical water
著者 (7件):
Sun Hongying
(School of Mechanical Engineering, Anyang Institute of Technology, Anyang 455002, China)
,
Yang Haijie
(Modern Engineering Training Center, Anyang Institute of Technology, Anyang 455002, China)
,
Wang Man
(School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China)
,
Giron-Palomares Benjamin
(School of Mechanical Engineering, Anyang Institute of Technology, Anyang 455002, China)
,
Zhou Zhangjian
(School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China)
,
Zhang Lefu
(School of Nuclear Science and Engineering, Shanghai Jiaotong University, No 800 Dongchuan Road, Shanghai, China)
,
Zhang Guangming
(School of Automobile & Transportation, Qingdao Technological University, Qingdao 266520, China)
資料名:
Journal of Nuclear Materials
(Journal of Nuclear Materials)
巻:
484
ページ:
339-346
発行年:
2017年
JST資料番号:
D0148A
ISSN:
0022-3115
資料種別:
逐次刊行物 (A)
記事区分:
原著論文
発行国:
オランダ (NLD)
言語:
英語 (EN)