溶体化処理中のその場TiB_2/Al複合材料のミクロ組織安定性【Powered by NICT】
Microstructural stability of in-situ TiB2/Al composite during solution treatment
著者 (8件):
Geng Jiwei
(State Key Laboratory of Metal Matrix Composites, School of Materials Science & Engineering, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China)
,
Hong Tianran
(School of Materials Science & Engineering, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China)
,
Shen Yanwei
(State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China)
,
Liu Gen
(School of Materials Science & Engineering, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China)
,
Xia Cunjuan
(State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China)
,
Chen Dong
(School of Materials Science & Engineering, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China)
,
Wang Minliang
(State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China)
,
Wang Haowei
(School of Materials Science & Engineering, State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China)
資料名:
Materials Characterization
(Materials Characterization)
巻:
124
ページ:
50-57
発行年:
2017年
JST資料番号:
D0448C
ISSN:
1044-5803
資料種別:
逐次刊行物 (A)
記事区分:
原著論文
発行国:
アメリカ合衆国 (USA)
言語:
英語 (EN)