文献
J-GLOBAL ID:202202249747175829
整理番号:22A0568242
高温クリープ中の[111]配向ニッケル基単結晶超合金の微細構造発達と変形機構【JST・京大機械翻訳】
Microstructure evolution and deformation mechanism of a [111]-oriented nickel-based single-crystal superalloy during high-temperature creep
著者 (7件):
Wang Guangyan
(School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, 110870, China)
,
Wang Guangyan
(Guizhou Laboratory of Reliability Evaluation of Metal Material Under Specific Environment, Guizhou University of Engineering Science, Bijie, 551700, China)
,
Zhang Song
(School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, 110870, China)
,
Tian Sugui
(School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, 110870, China)
,
Tian Ning
(Guizhou Laboratory of Reliability Evaluation of Metal Material Under Specific Environment, Guizhou University of Engineering Science, Bijie, 551700, China)
,
Zhao Guoqi
(School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, 110870, China)
,
Yan Huajin
(Guizhou Laboratory of Reliability Evaluation of Metal Material Under Specific Environment, Guizhou University of Engineering Science, Bijie, 551700, China)
資料名:
Journal of Materials Research and Technology
(Journal of Materials Research and Technology)
巻:
16
ページ:
495-504
発行年:
2022年
JST資料番号:
W3532A
ISSN:
2238-7854
資料種別:
逐次刊行物 (A)
記事区分:
原著論文
発行国:
オランダ (NLD)
言語:
英語 (EN)