圧縮機ブレード用TC17チタン合金の疲労挙動に及ぼす欠陥の影響:亀裂発生と疲労強度のモデリング【JST・京大機械翻訳】
Effects of defects on fatigue behavior of TC17 titanium alloy for compressor blades: Crack initiation and modeling of fatigue strength
著者 (7件):
Chi Weiqian
(Key Laboratory of Vehicle Advanced Manufacturing, Measuring and Control Technology (Beijing Jiaotong University), Ministry of Education, Beijing 100044, China)
,
Wang Wenjing
(Key Laboratory of Vehicle Advanced Manufacturing, Measuring and Control Technology (Beijing Jiaotong University), Ministry of Education, Beijing 100044, China)
,
Xu Wei
(Key Laboratory of Aeronautical Materials Testing and Evaluation, Aero Engine Corporation of China, Beijing Key Laboratory of Aeronautical Materials Testing and Evaluation, Beijing Institute of Aeronautical Materials, Beijing 100095, China)
,
Li Gen
(State Key Laboratory of Nonlinear Mechanics, Institute of Mechanics, Chinese Academy of Sciences, Beijing 100190, China)
,
Chen Xin
(Key Laboratory of Aeronautical Materials Testing and Evaluation, Aero Engine Corporation of China, Beijing Key Laboratory of Aeronautical Materials Testing and Evaluation, Beijing Institute of Aeronautical Materials, Beijing 100095, China)
,
Sun Chengqi
(State Key Laboratory of Nonlinear Mechanics, Institute of Mechanics, Chinese Academy of Sciences, Beijing 100190, China)
,
Sun Chengqi
(School of Engineering Science, University of Chinese Academy of Sciences, Beijing 100049, China)
資料名:
Engineering Fracture Mechanics
(Engineering Fracture Mechanics)
巻:
259
ページ:
Null
発行年:
2022年
JST資料番号:
A0119A
ISSN:
0013-7944
資料種別:
逐次刊行物 (A)
記事区分:
原著論文
発行国:
イギリス (GBR)
言語:
英語 (EN)