Al-Si-CuとAl-Si-Mg合金の引張特性の検討 β-鉄金属間化合物と気孔の影響

A study of tensile properties in Al-Si-Cu and Al-Si-Mg alloys: Effect of β-iron intermetallics and porosity

著者 (5件)： MA Z. (Dep. des sciences appliquees, Univ. du Quebec a Chicoutimi, Chicoutimi, Quebec, Canada G7H 2B1) ,  SAMUEL A.m. (Dep. des sciences appliquees, Univ. du Quebec a Chicoutimi, Chicoutimi, Quebec, Canada G7H 2B1) ,  SAMUEL F.h. (Dep. des sciences appliquees, Univ. du Quebec a Chicoutimi, Chicoutimi, Quebec, Canada G7H 2B1) ,  DOTY H.w. (Materials Engineering, GM Powertrain Group, Metal Casting Technol., Inc., Milford, NH 03055, USA) ,  VALTIERRA S. (Res. and Dev., Corporativo Nemak, S.A. de C.V., P.O. Box 100, Bosques del Valle, Garza Garcia 66221, N.L., MEX)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 490  号： 1-2  ページ： 36-51  発行年： 2008年08月25日 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： この検討では,実験用および工業用319.2合金と工業用A356.2合金を用いて,鋳造Al-Si-CuとAl-Si-Mg合金の引張り性質に及ぼすβ-鉄金属間化合物と気孔の影響を調べた。実験結果は,合金の延性と最大引張強さ(UTS)はβ-鉄金属間化合物のサイズの増加の結果として低下する,β-鉄金属間化合物長さ319.2合金では~100μm,A356.2合金では~70μmで最も顕著であった。気孔のサイズの増加も合金の延性とUTSに有害であった。今回の検討では,UTS対log伸びのプロットによって引張特性を解釈できるが,全ての試料条件での性質はlogUTS対log伸びのプロットによって最もよく解釈できる,ここでは低冷却速度の条件-高Feと高冷却速度-低Feの条件の間で性質は直線的に上昇した。結果は,得られたβ-Al₅FeSi小板サイズと気孔の値によって説明される。Copyright 2008 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *アルミニウム合金 ,  ケイ素含有合金 ,  銅含有合金 ,  マグネシウム含有合金 ,  *機械的性質 ,  金属間化合物 ,  気泡欠陥 ,  サイズ効果 ,  引張強さ ,  伸び ,  冷却速度 ,  鉄化合物

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (8件)： Al ,  Si ,  Cu ,  Mg合金 ,  引張特性 ,  鉄 ,  金属間化合物 ,  気孔